Ultramid? HMG13 HS BK-102|PA6-GF63|BASF

Product TextsUltramid? HMG13 HS BK-102 is a 63% glass filled, injection molding, high modulus Polyamid designed to have high strength and stiffness for metal replacement applications.It also has excellent moldability and outstanding surface appearance.

機械性能(機械性能(Mechanical properties))	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	22400 / 13400	MPa	ISO 527-1/-2
破壞時應變(Stress at break)	245 / -	MPa	ISO 527-1/-2
破壞時應變(Strain at break)	2 / -	%	ISO 527-1/-2

熱性能(熱性能(Thermal properties))	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
熔化溫度(熔化溫度(Melting temperature)) (10°C/min)	220 / *	°C	ISO 11357-1/-3
溫度負荷變形(Temp. of deflection under load) (1.80 MPa)	214 / *	°C	ISO 75-1/-2
燃燒性(球壓痕硬度(Burning behav)). at 1.5 mm nom. thickn.	HB / *	class	IEC 60695-11-10
厚度測試(Thickness tested)	1.5 / *	mm	IEC 60695-11-10
UL 識別(recognition)	UL / *	-	-
燃燒性(球壓痕硬度(Burning behav)). at thickness h	HB / *	class	IEC 60695-11-10
厚度測試(Thickness tested)	3.0 / *	mm	IEC 60695-11-10
UL 識別(recognition)	UL / *	-	-

其他屬性(Other properties)	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
密度(Density)	1740 / -	kg/m3	ISO 1183

Diagrams Water content: 0.03% A dehumidifying or desiccant dryer operating at 80 °C (176 °F) is recommended. Drying time is dependent on moisture level. Alternatively, please contact your BASF representative. Packing pressure affects the final part and can be used effectively in controlling sink marks and shrinkage. It should be applied and maintained until the gate area is completely frozen off.A maximum of 3.5 bar (50 psi) is recommended to minimize glass fiber breakage. Surface appearance is directly affected by injection rate.DisclaimerCopyright M-Base .