Ultramid? 8350 HS|PA6|BASF

Ultramid? 8350 HS|PA6|BASF 物性表: Ultramid? 8350 HS|PA6|BASF物性表及特性介紹,Ultramid? 8350 HS|PA6|BASF注塑參數詳情,如需Ultramid? 8350 HS|PA6|BASF下載, 可到相關下載區下載

Product TextsUltramid? 8350 HS is a heat stabilized, impact modified type 6 graft copolymer developed for extrusion, tubing, and jacketing applications requiring a high level of toughness combined with a moderate level of flexibility. It is also available in non-heat stabilized (Ultramid? 8350) and/or pigmented versions.

機械性能(機械性能(Mechanical properties))	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	1800 / 675	MPa	ISO 527-1/-2
屈服應力(Yield stress)	53 / 32	MPa	ISO 527-1/-2
屈服應變(Yield strain)	5 / 9	%	ISO 527-1/-2
斷裂拉伸應變(Nominal strain at break)	>50 / >50	%	ISO 527-1/-2
簡支梁沖擊強度(Charpy impact strength) (+23°C)	N / -	kJ/m2	ISO 179/1eU
簡支梁缺口沖擊強度(Charpy notched impact strength) (+23°C)	100 / -	kJ/m2	ISO 179/1eA

熱性能(熱性能(Thermal properties))	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
熔化溫度(熔化溫度(Melting temperature)) (10°C/min)	220 / *	°C	ISO 11357-1/-3
溫度負荷變形(Temp. of deflection under load) (1.80 MPa)	51 / *	°C	ISO 75-1/-2
燃燒性(球壓痕硬度(Burning behav)). at thickness h	HB / *	class	IEC 60695-11-10
厚度測試(Thickness tested)	3.0 / *	mm	IEC 60695-11-10
UL 識別(recognition)	UL / *	-	-

電氣性能(Electrical properties)	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
體積電阻率(Volume resistivity)	>1E13 / -	Ohm*m	IEC 60093
相比漏電起痕指數(Comparative tracking index)	- / 600	-	IEC 60112

其他屬性(Other properties)	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
吸水率(Water absorption)	6.7 / *	%	Sim. to ISO 62
吸濕性(Humidity absorption)	1.9 / *	%	Sim. to ISO 62
密度(Density)	1070 / *	kg/m3	ISO 1183

Test specimen production	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
Injection Molding, melt temperature	280	°C	ISO 294
Injection Molding, mold temperature	70	°C	ISO 10724

Diagrams Water content: 0.1%If drying becomes necessary, a dehumidifying or desiccant dryer operating at 80 degC (176 degF) is recommended.Drying time is dependent on moisture level.5:1 to 4.0:1 1.5-2.0:1In general, the ratio of die size to finished tube diameter is about 1.5-2.0:1.The mandrel (pin) size is determined the same way in relation to the inner tube diameter.For larger diameters, a differential pressure vacuum tank The vacuum sizer entrance should be about 3-9% larger than the finished tube outer diameter. Selection will depend on melt viscosity and die swell of the extrudate.39") O.D., open tank quenching with normal tap water is suggested.Depending upon line speed, quenching distance can vary from 5 to 12 meters (24.6-39.4 feet).A short air gap (die to quench water) is recommended for both tubing and cable jacketing for best flexibility.DisclaimerCopyright M-Base .

關鍵詞:
PA6
BASF
Ultramid? 8350 HS