Tarnamid? T-27 MHLS|PA6|Grupa Azoty

Tarnamid? T-27 MHLS|PA6|Grupa Azoty 物性表: Tarnamid? T-27 MHLS|PA6|Grupa Azoty物性表及特性介紹,Tarnamid? T-27 MHLS|PA6|Grupa Azoty注塑參數詳情,如需Tarnamid? T-27 MHLS|PA6|Grupa Azoty下載, 可到相關下載區下載

流變性能(Rheological properties)	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據
熔體體積流動速率(Melt volume-flow rate) (MVR)	100 / *	cm3/10min	ISO 1133
溫度(Temperature)	275 / *	°C	ISO 1133
負載(Load)	5 / *	kg	ISO 1133
成型收縮(Molding shrinkage) (parallel)	1.6 / *	%	ISO 294-4, 2577
成型收縮(Molding shrinkage) (normal)	1.8 / *	%	ISO 294-4, 2577

機械性能(機械性能(Mechanical properties))	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據
球壓痕硬度(Ball indentation hardness)	150 / 75	MPa	ISO 2039-1

熱性能(熱性能(Thermal properties))	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據
熔化溫度(熔化溫度(Melting temperature)) (10°C/min)	221 / *	°C	ISO 11357-1/-3
溫度負荷變形(Temp. of deflection under load) (1.80 MPa)	60 / *	°C	ISO 75-1/-2
維卡軟化溫度（50℃/ h的50N）Vicat softening temperature	195 / *	°C	ISO 306
COEFF線性熱(Coeff. of linear therm. expansion) (parallel)	90 / *	E-6/K	ISO 11359-1/-2
COEFF線性熱(Coeff. of linear therm. expansion) (normal)	120 / *	E-6/K	ISO 11359-1/-2
Burning behav. at 1.5 mm nom. thickn.	HB / *	class	IEC 60695-11-10
厚度測試(Thickness tested)	1.6 / *	mm	IEC 60695-11-10
燃燒性厚度(Burning behav. at thickness h)	HB / *	class	IEC 60695-11-10
厚度測試(Thickness tested)	3.2 / *	mm	IEC 60695-11-10

電氣性能(Electrical properties)	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據
相對介電常數(Relative permittivity) (1MHz)	3.5 / 4.2	-	IEC 60250
耗散因數(耗散因數(Dissipation factor)) (1MHz)	180 / 1000	E-4	IEC 60250
體積電阻率(Volume resistivity)	1E13 / 1E10	Ohm*m	IEC 60093
表面電阻率(Surface resistivity)	* / 1E13	Ohm	IEC 60093
電氣強度(Electric strength)	30 / 24	kV/mm	IEC 60243-1
相比漏電起痕指數(Comparative tracking index)	600 / 600	-	IEC 60112

其他屬性(Other properties)	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據
吸水率(Water absorption)	9.5 / *	%	Sim. to ISO 62
吸濕性(Humidity absorption)	3 / *	%	Sim. to ISO 62
密度(Density)	1140 / -	kg/m3	ISO 1183

CharacteristicsProcessingInjection MoldingDelivery formGranules, Black, WhiteSpecial CharacteristicsU.V. stabilized or stable to weather, Heat stabilized or stable to heatApplicationsAutomotive, Building Construction, Electrical and ElectronicalRegional AvailabilityEuropeDisclaimerCopyright M-Base .