SCHULAMID? 6 MKF 3010 HI|PA6-I-(MD+GF)30|A. Schulman

Schulman Product Texts20% mineral filled and 10% glass fibre reinforced PA 6 with increased impact strength6 / *	%	ISO 294-4, 2577
成型收縮(Molding shrinkage) (normal)	0.7 / *	%	ISO 294-4, 2577

機械性能(機械性能(Mechanical properties))	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	4500 / 3000	MPa	ISO 527-1/-2
破壞時應變(Stress at break)	65 / 50	MPa	ISO 527-1/-2
破壞時應變(Strain at break)	8 / 11	%	ISO 527-1/-2
簡支梁沖擊強度(Charpy impact strength) (+23°C)	45 / 68	kJ/m2	ISO 179/1eU
簡支梁缺口沖擊強度(Charpy notched impact strength) (+23°C)	6 / 16	kJ/m2	ISO 179/1eA

熱性能(熱性能(Thermal properties))	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
熔化溫度(熔化溫度(Melting temperature)) (10°C/min)	221 / *	°C	ISO 11357-1/-3
玻璃化轉變溫度(Glass transition temperature) (10°C/min)	42 / *	°C	ISO 11357-1/-2
溫度負荷變形(Temp. of deflection under load) (1.80 MPa)	155 / *	°C	ISO 75-1/-2
溫度負荷變形(Temp. of deflection under load) (0.45 MPa)	190 / *	°C	ISO 75-1/-2
維卡軟化溫度（50℃/ h的50N）Vicat softening temperature	195 / *	°C	ISO 306
燃燒性(球壓痕硬度(Burning behav)). at 1.5 mm nom. thickn.	HB / *	class	IEC 60695-11-10
厚度測試(Thickness tested)	1.5 / *	mm	IEC 60695-11-10

電氣性能(Electrical properties)	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
體積電阻率(Volume resistivity)	>1E13 / 1E10	Ohm*m	IEC 60093
表面電阻率(Surface resistivity)	* / >1E15	Ohm	IEC 60093
相比漏電起痕指數(Comparative tracking index)	- / 550	-	IEC 60112

其他屬性(Other properties)	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
密度(Density)	1330 / -	kg/m3	ISO 1183

流變計算屬性(Rheological calculation properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
噴射溫度(Ejection temperature)	120	°C	-

Test specimen production	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
Processing conditions acc. ISO	1870	-	ISO ....-2
Injection Molding, melt temperature	250	°C	ISO 294
Injection Molding, mold temperature	80	°C	ISO 10724
Injection Molding, injection velocity	250	mm/s	ISO 294
Injection Molding, pressure at hold	70	MPa	ISO 294

CharacteristicsProcessingInjection MoldingDelivery formGranulesAdditivesRelease agent, PlasticizerSpecial CharacteristicsHigh impact or impact modifiedRegional AvailabilityNorth America, Europe, Asia Pacific, South and Central America, Near East/AfricaOther text informationInjection moldingPREPROCESSINGPretreatment .
[/td][/tr][/table]