Stat-kon MS000IL|PP-MF(Fe)|SABIC_IP

加工/物理特性	值(Value)	單位(Unit)	測試標準(Test Standard)
ASTM數據(ASTM Data)
模具收縮(Mold Shrinkage) (MD)	0.013	mm/mm	ASTM D 955
模具收縮(Mold Shrinkage) (TD)	0.014	mm/mm	ASTM D 955
密度(Density) (73°F)	960	kg/m3	ASTM D 792

流變性能(Rheological properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據
成型收縮(Molding shrinkage) (parallel)	1.3	%	ISO 294-4, 2577
成型收縮(Molding shrinkage) (normal)	1.4	%	ISO 294-4, 2577

機械性能(機械性能(Mechanical properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據
拉伸模量(Tensile Modulus)	1170	MPa	ISO 527-1/-2
屈服應力(Yield stress)	20	MPa	ISO 527-1/-2
屈服應變(Yield strain)	5.6	%	ISO 527-1/-2
破壞時應變(Stress at break)	16	MPa	ISO 527-1/-2
破壞時應變(Strain at break)	38.9	%	ISO 527-1/-2
彎曲彈性模量(Flexural modulus) (23°C)	1180	MPa	ISO 178
懸臂梁式沖擊切口 (23°C)	10	kJ/m2	ISO 180/1A
懸臂梁式沖擊無切口(Izod Impact unnotched) (23°C)	N	kJ/m2	ISO 180/1U
ASTM數據(ASTM Data)
拉伸模量(Tensile Modulus)	1260	MPa	ASTM D 638
抗拉強度(Tensile Strength) at Yield	21	MPa	ASTM D 638
抗拉強度(Tensile Strength) at Break	15	MPa	ASTM D 638
屈服伸長率(Elongation at Yield)	7.1	%	ASTM D 638
斷裂伸長率(Elongation at Break)	76	%	ASTM D 638
彎曲彈性模量(彎曲彈性模量(Flexural Modulus))	1270	MPa	ASTM D 790
抗彎強度(Flexural Strength)	27	MPa	ASTM D 790
懸臂梁式沖擊切口 (1/8 in)	0.096	kJ/m	ASTM D 256

熱性能(熱性能(Thermal properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據
溫度負荷變形(Temp. of deflection under load) (1.80 MPa)	52	°C	ISO 75-1/-2
COEFF線性熱(Coeff. of linear therm. expansion) (parallel)	101	E-6/K	ISO 11359-1/-2
COEFF線性熱(Coeff. of linear therm. expansion) (normal)	117	E-6/K	ISO 11359-1/-2
ASTM數據(ASTM Data)
熱膨脹系數(Coefficient of Thermal Expansion) (MD)	99	E-6/K	ASTM D 696
熱膨脹系數(Coefficient of Thermal Expansion) (TD)	117	E-6/K	ASTM D 696
DTUL @ 264 psi	52	°C	ASTM D 648

電氣性能(Electrical properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ASTM數據(ASTM Data)
表面電阻率(Surface Resistivity)	1000000	Ohm	ASTM D 257

其他屬性(Other properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據
密度(Density)	960	kg/m3	ISO 1183

CharacteristicsProcessingInjection MoldingSpecial CharacteristicsIncreased electrical conductivity, High impact or impact modifiedRegional AvailabilityNorth America, South and Central AmericaDisclaimerCopyright M-Base .