Haiplen EP50 X2|PP|Taro Plast

Haiplen EP50 X2|PP|Taro Plast 物性表: Haiplen EP50 X2|PP|Taro Plast物性表及特性介紹,Haiplen EP50 X2|PP|Taro Plast注塑參數詳情,如需Haiplen EP50 X2|PP|Taro Plast下載, 可到相關下載區下載

流變性能(Rheological properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據
熔體流動指數(熔體流動指數(Melt flow index)) (MFI)	10	g/10min	ISO 1133
MFI溫度(MFI temperature)	230	°C	ISO 1133
MFI負載(MFI load)	2.16	kg	ISO 1133

機械性能(機械性能(Mechanical properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據
屈服應力(Yield stress)	30	MPa	ISO 527-1/-2
破壞時應變(Strain at break)	>50	%	ISO 527-1/-2
彎曲彈性模量(Flexural modulus) (23°C)	1100	MPa	ISO 178
ASTM數據(ASTM Data)
懸臂梁式沖擊切口 (1/8 in)	0.2	kJ/m	ASTM D 256
懸臂梁式沖擊切口 (Low-溫度(Temperature))	0.06	kJ/m	ASTM D 256
溫度(Temperature)	-20	°C	ASTM D 256

熱性能(熱性能(Thermal properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據
溫度負荷變形(Temp. of deflection under load) (1.80 MPa)	55	°C	ISO 75-1/-2
溫度負荷變形(Temp. of deflection under load) (0.45 MPa)	100	°C	ISO 75-1/-2
Vicat softening temperature A	142	°C	ISO 306
維卡軟化溫度（50℃/ h的50N）Vicat softening temperature	70	°C	ISO 306
燃燒性厚度(Burning behav. at thickness h)	V-2	class	IEC 60695-11-10
厚度測試(Thickness tested)	3.2	mm	IEC 60695-11-10
ASTM數據(ASTM Data)
UL 94 阻燃等級(Flame rating)	V-2	-	UL 94
厚度測試(Thickness tested)	1.6	mm	-
極限氧指數(Limiting 氧指數(Oxygen Index))	26	%	ASTM D 2863

電氣性能(Electrical properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據
相比漏電起痕指數(Comparative tracking index)	600	-	IEC 60112

其他屬性(Other properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據
吸水率(Water absorption)	0.05	%	Sim. to ISO 62
密度(Density)	950	kg/m3	ISO 1183

CharacteristicsSpecial CharacteristicsFlame retardant, U.V. stabilized or stable to weather, Heat stabilized or stable to heatFeaturesLaser Markable, Low Odor, CopolymerApplicationsAutomotive, Electrical and ElectronicalRegional AvailabilityEuropeDisclaimerCopyright M-Base .

關鍵詞:
PP
Taro Plast
Haiplen EP50 X2

轉載請注明: 轉自中國塑膠原料之家 http://www.spnmy.cn/wuxingbiao/

本文鏈接: http://www.spnmy.cn/wuxingbiao/show-87135.html

免責聲明: 本文 Haiplen EP50 X2|PP|Taro Plast 僅代表作者個人觀點，中國塑膠原料之家無關。中國塑膠原料之家網所轉載的內容，其版權均由原作者和資料提供方所擁有！如因作品版權問題需要處理，請與我們聯絡