Haiplen H50 T8|PP-T40|Taro Plast

Haiplen H50 T8|PP-T40|Taro Plast 物性表: Haiplen H50 T8|PP-T40|Taro Plast物性表及特性介紹,Haiplen H50 T8|PP-T40|Taro Plast注塑參數詳情,如需Haiplen H50 T8|PP-T40|Taro Plast下載, 可到相關下載區下載

流變性能(Rheological properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據
熔體流動指數(熔體流動指數(Melt flow index)) (MFI)	10	g/10min	ISO 1133
MFI溫度(MFI temperature)	230	°C	ISO 1133
MFI負載(MFI load)	2.16	kg	ISO 1133

機械性能(機械性能(Mechanical properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據
拉伸模量(Tensile Modulus)	4100	MPa	ISO 527-1/-2
屈服應力(Yield stress)	31	MPa	ISO 527-1/-2
屈服應變(Yield strain)	3.5	%	ISO 527-1/-2
破壞時應變(Stress at break)	27	MPa	ISO 527-1/-2
破壞時應變(Strain at break)	25	%	ISO 527-1/-2
簡支梁缺口沖擊強度(Charpy notched impact strength) (+23°C)	4	kJ/m2	ISO 179/1eA
彎曲彈性模量(Flexural modulus) (23°C)	4000	MPa	ISO 178
ASTM數據(ASTM Data)
懸臂梁式沖擊切口 (1/8 in)	0.03	kJ/m	ASTM D 256
懸臂梁式沖擊切口 (Low-溫度(Temperature))	0.02	kJ/m	ASTM D 256
溫度(Temperature)	-20	°C	ASTM D 256

熱性能(熱性能(Thermal properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據
溫度負荷變形(Temp. of deflection under load) (1.80 MPa)	85	°C	ISO 75-1/-2
Vicat softening temperature A	155	°C	ISO 306
維卡軟化溫度（50℃/ h的50N）Vicat softening temperature	100	°C	ISO 306
COEFF線性熱(Coeff. of linear therm. expansion) (parallel)	60	E-6/K	ISO 11359-1/-2
ASTM數據(ASTM Data)
UL 94 阻燃等級(Flame rating)	HB	-	UL 94
厚度測試(Thickness tested)	1.6	mm	-

其他屬性(Other properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據
吸水率(Water absorption)	0.05	%	Sim. to ISO 62
密度(Density)	1240	kg/m3	ISO 1183

CharacteristicsDelivery formPelletsSpecial CharacteristicsU.V. stabilized or stable to weather, Heat stabilized or stable to heatFeaturesLaser Markable, Low Odor, HomopolymerApplicationsAutomotive, Electrical and ElectronicalRegional AvailabilityEuropeDisclaimerCopyright M-Base .

關鍵詞:
Taro Plast
PP-T40
Haiplen H50 T8