SCHULADUR? A GF 30 HF2 FR1|PBT-GF30 FR|A. Schulman

Schulman Product TextsFlame retardant halogenated PBTstandard grade reinforced with 30% glass fibre; without PBDE; high flow.

流變性能(Rheological properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
熔體體積流動速率(Melt volume-flow rate) (MVR)	40	cm3/10min	ISO 1133
溫度(Temperature)	260	°C	ISO 1133
負載(Load)	5	kg	ISO 1133

機械性能(機械性能(Mechanical properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	12000	MPa	ISO 527-1/-2
破壞時應變(Stress at break)	150	MPa	ISO 527-1/-2
破壞時應變(Strain at break)	2.5	%	ISO 527-1/-2
簡支梁沖擊強度(Charpy impact strength) (+23°C)	60	kJ/m2	ISO 179/1eU
簡支梁沖擊強度(Charpy impact strength) (-30°C)	55	kJ/m2	ISO 179/1eU
簡支梁缺口沖擊強度(Charpy notched impact strength) (+23°C)	10	kJ/m2	ISO 179/1eA
簡支梁缺口沖擊強度(Charpy notched impact strength) (-30°C)	9	kJ/m2	ISO 179/1eA

熱性能(熱性能(Thermal properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
溫度負荷變形(Temp. of deflection under load) (1.80 MPa)	205	°C	ISO 75-1/-2
溫度負荷變形(Temp. of deflection under load) (0.45 MPa)	220	°C	ISO 75-1/-2
維卡軟化溫度（50℃/ h的50N）Vicat softening temperature	205	°C	ISO 306
燃燒性(球壓痕硬度(Burning behav)). at 1.5 mm nom. thickn.	V-0	class	IEC 60695-11-10
厚度測試(Thickness tested)	1.5	mm	IEC 60695-11-10
燃燒性(球壓痕硬度(Burning behav)). at thickness h	V-0	class	IEC 60695-11-10
厚度測試(Thickness tested)	0.8	mm	IEC 60695-11-10

其他屬性(Other properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
密度(Density)	1620	kg/m3	ISO 1183

CharacteristicsProcessingInjection MoldingSpecial CharacteristicsFlame retardantRegional AvailabilityNorth America, Europe, Asia Pacific, South and Central America, Near East/AfricaDisclaimerCopyright M-Base .