SCHULADUR? A GF 30 HI|PBT-I-GF30|A. Schulman

Schulman Product Texts30% glass fibre reinforced impact modified PBT16

ISO 1133

機械性能(機械性能(Mechanical properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	8400	MPa	ISO 527-1/-2
破壞時應變(Stress at break)	110	MPa	ISO 527-1/-2
破壞時應變(Strain at break)	3.5	%	ISO 527-1/-2
簡支梁沖擊強度(Charpy impact strength) (+23°C)	66	kJ/m2	ISO 179/1eU
簡支梁缺口沖擊強度(Charpy notched impact strength) (+23°C)	12	kJ/m2	ISO 179/1eA

熱性能(熱性能(Thermal properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
熔化溫度(熔化溫度(Melting temperature)) (10°C/min)	230	°C	ISO 11357-1/-3
玻璃化轉變溫度(Glass transition temperature) (10°C/min)	22	°C	ISO 11357-1/-2
溫度負荷變形(Temp. of deflection under load) (1.80 MPa)	204	°C	ISO 75-1/-2
溫度負荷變形(Temp. of deflection under load) (0.45 MPa)	213	°C	ISO 75-1/-2
燃燒性(球壓痕硬度(Burning behav)). at 1.5 mm nom. thickn.	HB	class	IEC 60695-11-10
厚度測試(Thickness tested)	1.5	mm	IEC 60695-11-10

電氣性能(Electrical properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
相對介電常數(Relative permittivity) (100Hz)	3.9	-	IEC 60250
相對介電常數(Relative permittivity) (1MHz)	3.79	-	IEC 60250
耗散因數(耗散因數(Dissipation factor)) (100Hz)	0.0019	E-4	IEC 60250
耗散因數(耗散因數(Dissipation factor)) (1MHz)	0.0226	E-4	IEC 60250
體積電阻率(Volume resistivity)	>1E13	Ohm*m	IEC 60093
表面電阻率(Surface resistivity)	>1E15	Ohm	IEC 60093
電氣強度(Electric strength)	18.7	kV/mm	IEC 60243-1
相比漏電起痕指數(Comparative tracking index)	450	-	IEC 60112

其他屬性(Other properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
密度(Density)	1490	kg/m3	ISO 1183

Test specimen production	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
Processing conditions acc. ISO	7790	-	ISO ....-2
Injection Molding, melt temperature	260	°C	ISO 294
Injection Molding, mold temperature	80	°C	ISO 10724
Injection Molding, injection velocity	250	mm/s	ISO 294
Injection Molding, pressure at hold	70	MPa	ISO 294

CharacteristicsProcessingInjection MoldingDelivery formGranulesAdditivesRelease agent, PlasticizerSpecial CharacteristicsHigh impact or impact modifiedRegional AvailabilityNorth America, Europe, Asia Pacific, South and Central America, Near East/AfricaOther text informationInjection moldingPREPROCESSINGPretreatment .
[/td][/tr][/table]

轉載請注明: 轉自中國塑膠原料之家 http://www.spnmy.cn/wuxingbiao/

本文鏈接: http://www.spnmy.cn/wuxingbiao/show-84453.html

免責聲明: 本文 SCHULADUR? A GF 30 HI|PBT-I-GF30|A. Schulman 僅代表作者個人觀點，中國塑膠原料之家無關。中國塑膠原料之家網所轉載的內容，其版權均由原作者和資料提供方所擁有！如因作品版權問題需要處理，請與我們聯絡