Crastin? S650FR BK851|PBT|DuPont

Crastin? S650FR BK851|PBT|DuPont 物性表: Crastin? S650FR BK851|PBT|DuPont物性表及特性介紹,Crastin? S650FR BK851|PBT|DuPont注塑參數詳情,如需Crastin? S650FR BK851|PBT|DuPont下載, 可到相關下載區下載

流變性能(Rheological properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據
成型收縮(Molding shrinkage) (parallel)	1.8	%	ISO 294-4, 2577
成型收縮(Molding shrinkage) (normal)	1.6	%	ISO 294-4, 2577

機械性能(機械性能(Mechanical properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據
拉伸模量(Tensile Modulus)	3000	MPa	ISO 527-1/-2
屈服應力(Yield stress)	65	MPa	ISO 527-1/-2
屈服應變(Yield strain)	4.6	%	ISO 527-1/-2
斷裂拉伸應變(Nominal strain at break)	7.2	%	ISO 527-1/-2
破壞時應變(Strain at break)	9	%	ISO 527-1/-2
簡支梁沖擊強度(Charpy impact strength) (+23°C)	60	kJ/m2	ISO 179/1eU
簡支梁缺口沖擊強度(Charpy notched impact strength) (+23°C)	3.8	kJ/m2	ISO 179/1eA
簡支梁缺口沖擊強度(Charpy notched impact strength) (-30°C)	3.4	kJ/m2	ISO 179/1eA

熱性能(熱性能(Thermal properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據
熔化溫度(熔化溫度(Melting temperature)) (10°C/min)	225	°C	ISO 11357-1/-3
溫度負荷變形(Temp. of deflection under load) (1.80 MPa)	65	°C	ISO 75-1/-2
溫度負荷變形(Temp. of deflection under load) (0.45 MPa)	160	°C	ISO 75-1/-2
Burning behav. at 1.5 mm nom. thickn.	V-0	class	IEC 60695-11-10
厚度測試(Thickness tested)	1.5	mm	IEC 60695-11-10
燃燒性厚度(Burning behav. at thickness h)	V-0	class	IEC 60695-11-10
厚度測試(Thickness tested)	0.8	mm	IEC 60695-11-10
Oxygen index	30	%	ISO 4589-1/-2

其他屬性(Other properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據
密度(Density)	1460	kg/m3	ISO 1183

CharacteristicsProcessingInjection MoldingDelivery formPellets, BlackSpecial CharacteristicsFlame retardantRegional AvailabilityNorth America, Europe, Asia Pacific, South and Central America, Near East/AfricaDisclaimerCopyright M-Base .

關鍵詞:
PBT
DuPont
Crastin? S650FR BK851