BERGADUR? PB40TM-Y|PBT|PolyOne

BERGADUR? PB40TM-Y|PBT|PolyOne 物性表: BERGADUR? PB40TM-Y|PBT|PolyOne物性表及特性介紹,BERGADUR? PB40TM-Y|PBT|PolyOne注塑參數詳情,如需BERGADUR? PB40TM-Y|PBT|PolyOne下載, 可到相關下載區下載

Product TextsPBT, unreinforced of deflection under load (1.80 MPa)	53	°C	ISO 75-1/-2
溫度負荷變形(Temp. of deflection under load) (0.45 MPa)	108	°C	ISO 75-1/-2
COEFF線性熱(Coeff. of linear therm. expansion) (parallel)	180	E-6/K	ISO 11359-1/-2
COEFF線性熱(Coeff. of linear therm. expansion) (normal)	180	E-6/K	ISO 11359-1/-2
燃燒性(球壓痕硬度(Burning behav)). at 1.5 mm nom. thickn.	HB	class	IEC 60695-11-10
厚度測試(Thickness tested)	1.6	mm	IEC 60695-11-10
燃燒性(球壓痕硬度(Burning behav)). at thickness h	HB	class	IEC 60695-11-10
厚度測試(Thickness tested)	0.8	mm	IEC 60695-11-10

電氣性能(Electrical properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
相對介電常數(Relative permittivity) (1MHz)	3.3	-	IEC 60250
體積電阻率(Volume resistivity)	>1E13	Ohm*m	IEC 60093
表面電阻率(Surface resistivity)	>1E15	Ohm	IEC 60093
電氣強度(Electric strength)	26	kV/mm	IEC 60243-1
相比漏電起痕指數(Comparative tracking index)	500	-	IEC 60112

其他屬性(Other properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
吸水率(Water absorption)	0.45	%	Sim. to ISO 62
吸濕性(Humidity absorption)	0.18	%	Sim. to ISO 62
密度(Density)	1280	kg/m3	ISO 1183

Test specimen production	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
Injection Molding, melt temperature	240	°C	ISO 294
Injection Molding, mold temperature	80	°C	ISO 10724

CharacteristicsProcessingInjection MoldingDelivery formPelletsRegional AvailabilityEuropeOther text informationInjection moldingPREPROCESSING Water Content0,04% ISO 1817 Liquid F) (23°C)[/td][/tr][tr][td]Salt solutions[/td][/tr][tr][td] .
[/td][/tr][/table]

關鍵詞:
PBT
PolyOne
BERGADUR? PB40TM-Y