Arnite? TV4 244 SX|PBT-GF20 FR(17)|DSM

Product Texts20% Glass Reinforced, Flame Retardant3	kJ/m2	ISO 179/1eA
簡支梁缺口沖擊強度(Charpy notched impact strength) (-30°C)	4.3	kJ/m2	ISO 179/1eA

熱性能(熱性能(Thermal properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
熔化溫度(熔化溫度(Melting temperature)) (10°C/min)	225	°C	ISO 11357-1/-3
溫度負荷變形(Temp. of deflection under load) (1.80 MPa)	210	°C	ISO 75-1/-2
溫度負荷變形(Temp. of deflection under load) (0.45 MPa)	220	°C	ISO 75-1/-2
COEFF線性熱(Coeff. of linear therm. expansion) (parallel)	40	E-6/K	ISO 11359-1/-2
COEFF線性熱(Coeff. of linear therm. expansion) (normal)	80	E-6/K	ISO 11359-1/-2
燃燒性(球壓痕硬度(Burning behav)). at 1.5 mm nom. thickn.	V-0	class	IEC 60695-11-10
厚度測試(Thickness tested)	1.5	mm	IEC 60695-11-10
燃燒性(球壓痕硬度(Burning behav)). at thickness h	V-0	class	IEC 60695-11-10
厚度測試(Thickness tested)	0.8	mm	IEC 60695-11-10

電氣性能(Electrical properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
相對介電常數(Relative permittivity) (100Hz)	3.9	-	IEC 60250
相對介電常數(Relative permittivity) (1MHz)	3.7	-	IEC 60250
耗散因數(耗散因數(Dissipation factor)) (100Hz)	20	E-4	IEC 60250
耗散因數(耗散因數(Dissipation factor)) (1MHz)	150	E-4	IEC 60250
體積電阻率(Volume resistivity)	>1E13	Ohm*m	IEC 60093
電氣強度(Electric strength)	27	kV/mm	IEC 60243-1
相比漏電起痕指數(Comparative tracking index)	250	-	IEC 60112

其他屬性(Other properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
吸水率(Water absorption)	0.3	%	Sim. to ISO 62
吸濕性(Humidity absorption)	0.15	%	Sim. to ISO 62
密度(Density)	1610	kg/m3	ISO 1183

CharacteristicsProcessingInjection MoldingDelivery formPelletsAdditivesRelease agentSpecial CharacteristicsFlame retardantRegional AvailabilityAsia PacificOther text informationInjection moldingInjection Molding RecommendationsDisclaimerCopyright M-Base .
[/td][/tr][/table]

轉載請注明: 轉自中國塑膠原料之家 http://www.spnmy.cn/wuxingbiao/

本文鏈接: http://www.spnmy.cn/wuxingbiao/show-83249.html

免責聲明: 本文 Arnite? TV4 244 SX|PBT-GF20 FR(17)|DSM 僅代表作者個人觀點，中國塑膠原料之家無關。中國塑膠原料之家網所轉載的內容，其版權均由原作者和資料提供方所擁有！如因作品版權問題需要處理，請與我們聯絡