Zytel? 80G14AHS BK099|PA66-GF14|DuPont

流變性能(Rheological properties)	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據
成型收縮(Molding shrinkage) (parallel)	0.7 / *	%	ISO 294-4, 2577
成型收縮(Molding shrinkage) (normal)	0.9 / *	%	ISO 294-4, 2577

機械性能(機械性能(Mechanical properties))	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據
拉伸模量(Tensile Modulus)	5000 / -	MPa	ISO 527-1/-2
破壞時應變(Stress at break)	110 / -	MPa	ISO 527-1/-2
破壞時應變(Strain at break)	3.8 / -	%	ISO 527-1/-2
簡支梁沖擊強度(Charpy impact strength) (+23°C)	70 / -	kJ/m2	ISO 179/1eU
簡支梁缺口沖擊強度(Charpy notched impact strength) (+23°C)	13 / -	kJ/m2	ISO 179/1eA
彎曲彈性模量(Flexural modulus) (23°C)	4400 / -	MPa	ISO 178
懸臂梁式沖擊切口 (23°C)	13 / -	kJ/m2	ISO 180/1A
懸臂梁式沖擊切口	11 / -	kJ/m2	ISO 180/1A
溫度(Temperature)	0	°C	ISO 180/1A
懸臂梁式沖擊無切口(Izod Impact unnotched) (23°C)	55	kJ/m2	ISO 180/1U

熱性能(熱性能(Thermal properties))	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據
熔化溫度(熔化溫度(Melting temperature)) (10°C/min)	263 / *	°C	ISO 11357-1/-3
溫度負荷變形(Temp. of deflection under load) (1.80 MPa)	240 / *	°C	ISO 75-1/-2
溫度負荷變形(Temp. of deflection under load) (0.45 MPa)	258 / *	°C	ISO 75-1/-2
COEFF線性熱(Coeff. of linear therm. expansion) (parallel)	40 / *	E-6/K	ISO 11359-1/-2
COEFF線性熱(Coeff. of linear therm. expansion) (normal)	104 / *	E-6/K	ISO 11359-1/-2

其他屬性(Other properties)	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據
密度(Density)	1190 / -	kg/m3	ISO 1183

CharacteristicsProcessingInjection MoldingDelivery formPellets, BlackSpecial CharacteristicsHigh impact or impact modified, Heat stabilized or stable to heatFeaturesFatigue Resistance, Thermal StabilityChemical ResistanceGeneral Chemical Resistance, Grease Resistance, Oil ResistanceApplicationsAutomotive, Asia Pacific, South and Central America, Near East/AfricaDisclaimerCopyright M-Base .