Verton RV006ESV_GY7E071|PA66-GF30|SABIC_IP

加工/物理特性	值(Value)	單位(Unit)	測試標準(Test Standard)
ASTM數據(ASTM Data)
模具收縮(Mold Shrinkage) (MD)	0.0039	mm/mm	ASTM D 955
模具收縮(Mold Shrinkage) (TD)	0.011	mm/mm	ASTM D 955
密度(Density) (73°F)	1390	kg/m3	ASTM D 792

機械性能(機械性能(Mechanical properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據
拉伸模量(Tensile Modulus)	8320	MPa	ISO 527-1/-2
破壞時應變(Stress at break)	163	MPa	ISO 527-1/-2
破壞時應變(Strain at break)	2.3	%	ISO 527-1/-2
彎曲彈性模量(Flexural modulus) (23°C)	7750	MPa	ISO 178
懸臂梁式沖擊切口 (23°C)	13	kJ/m2	ISO 180/1A
懸臂梁式沖擊切口	14	kJ/m2	ISO 180/1A
溫度(Temperature)	-40	°C	ISO 180/1A
懸臂梁式沖擊無切口(Izod Impact unnotched) (23°C)	158	kJ/m2	ISO 180/1U
ASTM數據(ASTM Data)
拉伸模量(Tensile Modulus)	9110.03	MPa	ASTM D 638
抗拉強度(Tensile Strength) at Yield	162	MPa	ASTM D 638
抗拉強度(Tensile Strength) at Break	161	MPa	ASTM D 638
屈服伸長率(Elongation at Yield)	2.3	%	ASTM D 638
斷裂伸長率(Elongation at Break)	2.3	%	ASTM D 638
彎曲彈性模量(彎曲彈性模量(Flexural Modulus))	8650.01	MPa	ASTM D 790
懸臂梁式沖擊切口 (1/8 in)	0.057	kJ/m	ASTM D 256
懸臂梁式沖擊切口 (Low-溫度(Temperature))	0.052	kJ/m	ASTM D 256
溫度(Temperature)	-40	°C	ASTM D 256

熱性能(熱性能(Thermal properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據
溫度負荷變形(Temp. of deflection under load) (1.80 MPa)	256	°C	ISO 75-1/-2
溫度負荷變形(Temp. of deflection under load) (0.45 MPa)	261	°C	ISO 75-1/-2
ASTM數據(ASTM Data)
熱膨脹系數(Coefficient of Thermal Expansion) (MD)	33.7	E-6/K	ASTM D 696
熱膨脹系數(Coefficient of Thermal Expansion) (TD)	63.5	E-6/K	ASTM D 696
DTUL @ 66 psi	260	°C	ASTM D 648
DTUL @ 264 psi	256	°C	ASTM D 648

其他屬性(Other properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據
吸濕性(Humidity absorption)	1.2	%	Sim. to ISO 62
密度(Density)	1380	kg/m3	ISO 1183

CharacteristicsProcessingInjection MoldingDelivery formPelletsRegional AvailabilityNorth America, South and Central AmericaDisclaimerCopyright M-Base .