Ultramid? NFX-0102 NF2004|PA66-GF30|BASF

Product TextsUltramid? NFX-0102 NF2004 is a heat stabilized, 30% glass bead PA66 injection molding grade. It is especially formulated for low warp, increased stiffness and excellent dimensional stability.

機械性能(機械性能(Mechanical properties))	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	4500 / -	MPa	ISO 527-1/-2
破壞時應變(Stress at break)	70 / -	MPa	ISO 527-1/-2
破壞時應變(Strain at break)	2.5 / -	%	ISO 527-1/-2
簡支梁缺口沖擊強度(Charpy notched impact strength) (+23°C)	2.5 / -	kJ/m2	ISO 179/1eA

熱性能(熱性能(Thermal properties))	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
熔化溫度(熔化溫度(Melting temperature)) (10°C/min)	263 / *	°C	ISO 11357-1/-3
溫度負荷變形(Temp. of deflection under load) (1.80 MPa)	85 / *	°C	ISO 75-1/-2

其他屬性(Other properties)	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
密度(Density)	1360 / -	kg/m3	ISO 1183

CharacteristicsRegional AvailabilityNorth AmericaOther text informationInjection moldingPolyamid 66 materials must be properly dried in order to provide parts with optimum strength and toughness. Polyamid 66 materials are hygroscopic and will become degraded by excessive moisture during the injection molding process. For unopened bag/box, dry at 140F (60°C) for 1-2 hours. For material exposed to the atmosphere, if additional drying is needed, dry at 150F (66°C) or until the moisture level is between 0.04 - 0.20%.35 MPa (0 – 50 psi) Packing pressure affects the final part and can be used effectively in controlling sink marks and shrinkage. It should be applied and maintained until the gate area is completely frozen off.DisclaimerCopyright M-Base .