Ultramid? NBX-0025 NF2001|PA66|BASF

Ultramid? NBX-0025 NF2001|PA66|BASF 物性表: Ultramid? NBX-0025 NF2001|PA66|BASF物性表及特性介紹,Ultramid? NBX-0025 NF2001|PA66|BASF注塑參數詳情,如需Ultramid? NBX-0025 NF2001|PA66|BASF下載, 可到相關下載區下載

Product TextsUltramid? NBX-0025 NF2001 is a specialty, unfilled PA6/6.

機械性能(機械性能(Mechanical properties))	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	3000 / 1200	MPa	ISO 527-1/-2
屈服應力(Yield stress)	83 / 54	MPa	ISO 527-1/-2
屈服應變(Yield strain)	5 / 25	%	ISO 527-1/-2
斷裂拉伸應變(Nominal strain at break)	25 / >50	%	ISO 527-1/-2
簡支梁沖擊強度(Charpy impact strength) (+23°C)	N / N	kJ/m2	ISO 179/1eU
簡支梁沖擊強度(Charpy impact strength) (-30°C)	N / N	kJ/m2	ISO 179/1eU
簡支梁缺口沖擊強度(Charpy notched impact strength) (+23°C)	5.7 / 16	kJ/m2	ISO 179/1eA
簡支梁缺口沖擊強度(Charpy notched impact strength) (-30°C)	4 / 4	kJ/m2	ISO 179/1eA

熱性能(熱性能(Thermal properties))	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
熔化溫度(熔化溫度(Melting temperature)) (10°C/min)	257 / *	°C	ISO 11357-1/-3
溫度負荷變形(Temp. of deflection under load) (1.80 MPa)	72 / *	°C	ISO 75-1/-2
溫度負荷變形(Temp. of deflection under load) (0.45 MPa)	205 / *	°C	ISO 75-1/-2

其他屬性(Other properties)	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
吸水率(Water absorption)	8.5 / *	%	Sim. to ISO 62
吸濕性(Humidity absorption)	2.5 / *	%	Sim. to ISO 62
密度(Density)	1140 / -	kg/m3	ISO 1183

CharacteristicsRegional AvailabilityNorth AmericaOther text informationInjection moldingPA66 materials must be properly dried in order to provide parts with optimum strength and toughness. PA66 materials are hygroscopic and will become degraded by excessive moisture during the injection molding process. For unopened bag/box, dry at 140 F (60°C). For material exposed to the atmosphere, if additional drying time is needed, dry at 150 F (66°C) until the moisture level is between 0.04 and 0.20%. Do not overdry the resin.35 MPa (0 - 50 psi) Packing pressure affects the final part and can be used effectively in controlling sink marks and shrinkage. It should be applied and maintained until the gate area is completely frozen off.DisclaimerCopyright M-Base .