Technyl? A 216 V30 Natural FA|PA66-GF30|Rhodia

Product TextsPolyamide PA66 , reinforced with 30% of glass fibre and modified for enhanced injection moulding.

機械性能(機械性能(Mechanical properties))	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	10000 / 7500	MPa	ISO 527-1/-2
破壞時應變(Stress at break)	190 / 135	MPa	ISO 527-1/-2
破壞時應變(Strain at break)	3 / 4	%	ISO 527-1/-2
簡支梁沖擊強度(Charpy impact strength) (+23°C)	80 / 95	kJ/m2	ISO 179/1eU
簡支梁缺口沖擊強度(Charpy notched impact strength) (+23°C)	12 / 16	kJ/m2	ISO 179/1eA

熱性能(熱性能(Thermal properties))	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
熔化溫度(熔化溫度(Melting temperature)) (10°C/min)	263 / *	°C	ISO 11357-1/-3
溫度負荷變形(Temp. of deflection under load) (1.80 MPa)	255 / *	°C	ISO 75-1/-2
COEFF線性熱(Coeff. of linear therm. expansion) (normal)	25 / *	E-6/K	ISO 11359-1/-2

電氣性能(Electrical properties)	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
相對介電常數(Relative permittivity) (1MHz)	3.75 / 4	-	IEC 60250
耗散因數(耗散因數(Dissipation factor)) (1MHz)	100 / 110	E-4	IEC 60250
體積電阻率(Volume resistivity)	1E13 / 2E11	Ohm*m	IEC 60093
表面電阻率(Surface resistivity)	* / 1E12	Ohm	IEC 60093
電氣強度(Electric strength)	40 / 30	kV/mm	IEC 60243-1
相比漏電起痕指數(Comparative tracking index)	600 / 600	-	IEC 60112

其他屬性(Other properties)	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
吸水率(Water absorption)	0.8 / *	%	Sim. to ISO 62
密度(Density)	1370 / -	kg/m3	ISO 1183

Test specimen production	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
Injection Molding, mold temperature	80	°C	ISO 10724

Diagrams In the case that the virgin material has absorbed moisture, it must be dried to a final moisture content of less than 0,2% with a dehumidified air drying equipment at approx 80°C. .