Leona FR560|PA66|Asahi Kasei

Leona FR560|PA66|Asahi Kasei 物性表: Leona FR560|PA66|Asahi Kasei物性表及特性介紹,Leona FR560|PA66|Asahi Kasei注塑參數(shù)詳情,如需Leona FR560|PA66|Asahi Kasei下載, 可到相關(guān)下載區(qū)下載

加工/物理特性	值(Value)	單位(Unit)	測試標準(Test Standard)
ASTM數(shù)據(jù)(ASTM Data)
模具收縮(Mold Shrinkage) (MD)	0.01	mm/mm	ASTM D 955
模具收縮(Mold Shrinkage) (TD)	0.017	mm/mm	ASTM D 955
密度(Density) (73°F)	1160	kg/m3	ASTM D 792
吸水率(Water Absorption) (Equilibrium)	2.3	%	ASTM D 570

流變性能(Rheological properties)	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數(shù)據(jù)
成型收縮(Molding shrinkage) (parallel)	1.0 / *	%	ISO 294-4, 2577
成型收縮(Molding shrinkage) (normal)	1.7 / *	%	ISO 294-4, 2577

機械性能(機械性能(Mechanical properties))	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數(shù)據(jù)
拉伸模量(Tensile Modulus)	3700 / 1500	MPa	ISO 527-1/-2
屈服應(yīng)力(Yield stress)	86.2 / 57	MPa	ISO 527-1/-2
屈服應(yīng)變(Yield strain)	4.5 / 22	%	ISO 527-1/-2
破壞時應(yīng)變(Stress at break)	80.7 / -	MPa	ISO 527-1/-2
破壞時應(yīng)變(Strain at break)	20 / 50	%	ISO 527-1/-2
簡支梁沖擊強度(Charpy impact strength) (+23°C)	87 / N	kJ/m2	ISO 179/1eU
簡支梁缺口沖擊強度(Charpy notched impact strength) (+23°C)	5 / 9	kJ/m2	ISO 179/1eA
彎曲彈性模量(Flexural modulus) (23°C)	3200 / 1400	MPa	ISO 178
ASTM數(shù)據(jù)(ASTM Data)
抗拉強度(Tensile Strength)	84.1	MPa	ASTM D 638
斷裂伸長率(Elongation at Break)	8.8	%	ASTM D 638
彎曲彈性模量(彎曲彈性模量(Flexural Modulus))	3199.16	MPa	ASTM D 790
抗彎強度(Flexural Strength)	127	MPa	ASTM D 790
洛氏硬度(Rockwell Hardness)	R 120	-	ASTM D 785
懸臂梁式?jīng)_擊切口 (1/8 in)	0.032	kJ/m	ASTM D 256

熱性能(熱性能(Thermal properties))	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數(shù)據(jù)
溫度負荷變形(Temp. of deflection under load) (1.80 MPa)	77 / *	°C	ISO 75-1/-2
溫度負荷變形(Temp. of deflection under load) (0.45 MPa)	223 / *	°C	ISO 75-1/-2
Burning behav. at 1.5 mm nom. thickn.	V-0 / *	class	IEC 60695-11-10
燃燒性厚度(Burning behav. at thickness h)	V-0 / *	class	IEC 60695-11-10
厚度測試(Thickness tested)	3.0 / *	mm	IEC 60695-11-10
ASTM數(shù)據(jù)(ASTM Data)
UL 94 阻燃等級(Flame rating)	V-0	-	UL 94
厚度測試(Thickness tested)	1.5	mm	-
熱膨脹系數(shù)(Coefficient of Thermal Expansion) (MD)	70.2	E-6/K	ASTM D 696
DTUL @ 66 psi	240	°C	ASTM D 648
DTUL @ 264 psi	80	°C	ASTM D 648

電氣性能(Electrical properties)	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數(shù)據(jù)
相比漏電起痕指數(shù)(Comparative tracking index)	600 / 600	-	IEC 60112
ASTM數(shù)據(jù)(ASTM Data)
絕緣強度(Dielectric Strength) (Short Time)	22	kV/mm	ASTM D 149
表面電阻率(Surface Resistivity)	1E13	Ohm	ASTM D 257
體積電阻率(Volume Resistivity)	1E14	Ohm*cm	ASTM D 257
耐電弧性(Arc Resistance)	150	s	ASTM D 495

其他屬性(Other properties)	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數(shù)據(jù)
吸濕性(Humidity absorption)	2.3 / *	%	Sim. to ISO 62
密度(Density)	1160 / -	kg/m3	ISO 1183

CharacteristicsProcessingInjection MoldingDelivery formPelletsSpecial CharacteristicsFlame retardant, Heat stabilized or stable to heatChemical ResistanceSolvent Resistance, Oil ResistanceApplicationsAutomotive, Electrical and ElectronicalRegional AvailabilityNorth AmericaDisclaimerCopyright M-Base .

關(guān)鍵詞:
PA66
Asahi Kasei
Leona FR560

轉(zhuǎn)載請注明: 轉(zhuǎn)自中國塑膠原料之家 http://www.spnmy.cn/wuxingbiao/

本文鏈接: http://www.spnmy.cn/wuxingbiao/show-80927.html

免責聲明: 本文 Leona FR560|PA66|Asahi Kasei 僅代表作者個人觀點，中國塑膠原料之家無關(guān)。中國塑膠原料之家網(wǎng)所轉(zhuǎn)載的內(nèi)容，其版權(quán)均由原作者和資料提供方所擁有！如因作品版權(quán)問題需要處理，請與我們聯(lián)絡(luò)