Lubricomp KP002|(POM+PTFE+SI)|SABIC_IP

加工/物理特性	值(Value)	單位(Unit)	測試標準(Test Standard)
ASTM數據(ASTM Data)
模具收縮(Mold Shrinkage) (MD)	0.022	mm/mm	ASTM D 955
模具收縮(Mold Shrinkage) (TD)	0.022	mm/mm	ASTM D 955
密度(Density) (73°F)	1430	kg/m3	ASTM D 792

流變性能(Rheological properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據
成型收縮(Molding shrinkage) (parallel)	2.2	%	ISO 294-4, 2577
成型收縮(Molding shrinkage) (normal)	2.2	%	ISO 294-4, 2577

機械性能(機械性能(Mechanical properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據
拉伸模量(Tensile Modulus)	2330	MPa	ISO 527-1/-2
屈服應力(Yield stress)	46	MPa	ISO 527-1/-2
屈服應變(Yield strain)	29	%	ISO 527-1/-2
彎曲彈性模量(Flexural modulus) (23°C)	2000	MPa	ISO 178
懸臂梁式沖擊切口 (23°C)	5	kJ/m2	ISO 180/1A
懸臂梁式沖擊無切口(Izod Impact unnotched) (23°C)	74	kJ/m2	ISO 180/1U
ASTM數據(ASTM Data)
拉伸模量(Tensile Modulus)	2750	MPa	ASTM D 638
抗拉強度(Tensile Strength) at Yield	46	MPa	ASTM D 638
抗拉強度(Tensile Strength) at Break	46	MPa	ASTM D 638
屈服伸長率(Elongation at Yield)	26.3	%	ASTM D 638
斷裂伸長率(Elongation at Break)	40.9	%	ASTM D 638
彎曲彈性模量(彎曲彈性模量(Flexural Modulus))	2060	MPa	ASTM D 790
懸臂梁式沖擊切口 (1/8 in)	0.0509	kJ/m	ASTM D 256

熱性能(熱性能(Thermal properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據
溫度負荷變形(Temp. of deflection under load) (1.80 MPa)	87	°C	ISO 75-1/-2
溫度負荷變形(Temp. of deflection under load) (0.45 MPa)	146	°C	ISO 75-1/-2
COEFF線性熱(Coeff. of linear therm. expansion) (parallel)	106	E-6/K	ISO 11359-1/-2
COEFF線性熱(Coeff. of linear therm. expansion) (normal)	103	E-6/K	ISO 11359-1/-2
ASTM數據(ASTM Data)
熱膨脹系數(Coefficient of Thermal Expansion) (MD)	106	E-6/K	ASTM D 696
熱膨脹系數(Coefficient of Thermal Expansion) (TD)	103	E-6/K	ASTM D 696
DTUL @ 66 psi	156	°C	ASTM D 648
DTUL @ 264 psi	92	°C	ASTM D 648

其他屬性(Other properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據
密度(Density)	1430	kg/m3	ISO 1183

CharacteristicsProcessingInjection MoldingAdditivesLubricantsFeaturesCopolymerRegional AvailabilityNorth America, Asia Pacific, South and Central AmericaDisclaimerCopyright M-Base .

轉載請注明: 轉自中國塑膠原料之家 http://www.spnmy.cn/wuxingbiao/

本文鏈接: http://www.spnmy.cn/wuxingbiao/show-79219.html

免責聲明: 本文 Lubricomp KP002|(POM+PTFE+SI)|SABIC_IP 僅代表作者個人觀點，中國塑膠原料之家無關。中國塑膠原料之家網所轉載的內容，其版權均由原作者和資料提供方所擁有！如因作品版權問題需要處理，請與我們聯絡