RamTal PM1609|POM|Polyram

RamTal PM1609|POM|Polyram 物性表: RamTal PM1609|POM|Polyram物性表及特性介紹,RamTal PM1609|POM|Polyram注塑參數詳情,如需RamTal PM1609|POM|Polyram下載, 可到相關下載區下載

流變性能(Rheological properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據
成型收縮(Molding shrinkage) (parallel)	2.0	%	ISO 294-4, 2577
熔體流動指數(熔體流動指數(Melt flow index)) (MFI)	9	g/10min	ISO 1133
MFI溫度(MFI temperature)	190	°C	ISO 1133
MFI負載(MFI load)	2.16	kg	ISO 1133

機械性能(機械性能(Mechanical properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據
屈服應力(Yield stress)	65	MPa	ISO 527-1/-2
破壞時應變(Strain at break)	40	%	ISO 527-1/-2
彎曲彈性模量(Flexural modulus) (23°C)	2700	MPa	ISO 178
懸臂梁式沖擊切口 (23°C)	6	kJ/m2	ISO 180/1A
洛氏硬度(Rockwell hardness)	R 82	-	ISO 2039-2
ASTM數據(ASTM Data)
抗彎強度(Flexural Strength)	95	MPa	ASTM D 790

熱性能(熱性能(Thermal properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據
熔化溫度(熔化溫度(Melting temperature)) (10°C/min)	165	°C	ISO 11357-1/-3
溫度負荷變形(Temp. of deflection under load) (1.80 MPa)	110	°C	ISO 75-1/-2
溫度負荷變形(Temp. of deflection under load) (0.45 MPa)	160	°C	ISO 75-1/-2
燃燒性厚度(Burning behav. at thickness h)	HB	class	IEC 60695-11-10
厚度測試(Thickness tested)	3.0	mm	IEC 60695-11-10

電氣性能(Electrical properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據
相對介電常數(Relative permittivity) (1MHz)	3.8	-	IEC 60250
體積電阻率(Volume resistivity)	>1E13	Ohm*m	IEC 60093
表面電阻率(Surface resistivity)	1E14	Ohm	IEC 60093
電氣強度(Electric strength)	24	kV/mm	IEC 60243-1

其他屬性(Other properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據
吸水率(Water absorption)	0.22	%	Sim. to ISO 62
密度(Density)	1440	kg/m3	ISO 1183

CharacteristicsProcessingInjection MoldingDelivery formPelletsFeaturesLow OdorRegional AvailabilityNorth America, Europe, Asia Pacific, South and Central America, Near East/AfricaDisclaimerCopyright M-Base Engineering+Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from M-Base; this is especially valid for claims of compensation resulting from consequential damages. M-Base explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.

關鍵詞:
RamTal PM1609|POM|Polyram