PC/PET/RS1U/廣達塑料
- 生產(chǎn)企業(yè)： 廣達塑料
①原料描述部分
| 規(guī)格級別 | 透明 其它 注塑 | 外觀顏色 | |
|---|---|---|---|
| 該料用途 | |||
| 備注說明 | 汽車配件，醫(yī)療器材 | ||
②加工條件
| 加工條件 |
|---|
③原料技術(shù)數(shù)據(jù)
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 物理性能 | 比重 | -- | ASTM D792 | 1.20 | g/cm³ |
| -- | ISO 1183 | 1.17 | g/cm³ | ||
| 熔流率 | 265 ℃/2.16kg | ASTM D1238 | 15 | g/10 min | |
| 熔化體積流率 | MVR 265 ℃/2.16kg | ISO 1133 | 15.0 | cm³/10 min | |
| 收縮率 | 流動:3.20mm | Intemal Method | 0.5到0.8 | % | |
| 橫向流動:3.20mm | Intemal Method | 0.4到0.6 | % | ||
| 吸水率 | 飽和,23℃ | ISO 62 | 0.050 | % | |
| 平衡,23℃,50%RH | ISO 62 | 0.20 | % | ||
| 機械性能 | 拉伸模量 | --² | ASTM D638 | 1520 | MPa |
| -- | ISO 527-2/1 | 1600 | MPa | ||
| 抗張強度 | 屈服³ | ASTM D638 | 47.0 | MPa | |
| 屈服 | ISO 527-2/50 | 55.0 | MPa | ||
| 斷裂³ | ASTM D638 | 46.0 | MPa | ||
| 斷裂 | ISO 527-2/50 | 54.0 | MPa | ||
| 伸長率 | 屈服³ | ASTM D638 | 5.0 | % | |
| 屈服 | ISO 527-2/50 | ＞5.0 | % | ||
| 斷裂³ | ASTM D638 | 150 | % | ||
| 斷裂 | ISO 527-2/50 | ＞200 | % | ||
| 彎曲模量 | 50.0mm跨距4 | ASTM D790 | 1680 | MPa | |
| -- | ISO 178 | 1700 | MPa | ||
| 彎曲強度 | --5,6 | ISO 178 | 78.0 | MPa | |
| 屈服,50.0mm跨距4 | ASTM D790 | 71.0 | MPa | ||
| 沖擊性能 | 簡支梁缺口沖擊強度7 | 23℃ | ISO 179/1eA | 10 | kJ/㎡ |
| 懸壁梁缺口沖擊強度 | -30℃ | ASTM D256 | 73 | J/m | |
| 23℃ | ASTM D256 | 1100 | J/m | ||
| -30℃8 | ISO 180/1A | 7.0 | kJ/㎡ | ||
| -10℃8 | ISO 180/1A | 5.0 | kJ/㎡ | ||
| 23℃8 | ISO 180/1A | 8.0 | kJ/㎡ | ||
| 裝有測量儀表的落鏢沖擊 | 23℃，Total Energy | ASTM D3763 | 95.0 | J | |
| 硬度計硬度 | 支撐D,10秒 | ASTM D2240 | 74 | ||
| 熱性能 | 熱變形溫度 | 0.45MPa,未退火,3.20mm | ASTM D648 | 79.0 | ℃ |
| 1.8MPa,未退火,3.20mm | ASTM D648 | 75.0 | ℃ | ||
| 1.8MPa,未退火,100mm跨距9 | ISO 75-2/Ae | 80.0 | ℃ | ||
| 1.8MPa,未退火,64.0mm跨距10 | ISO 75-2/Af | 78.0 | ℃ | ||
| 維卡軟化溫度 | -- | ASTM D152511 | 91.0 | ℃ | |
| -- | ISO 306/B120 | 96.0 | ℃ | ||
| Ball Pressure Test | 85 ℃ | IEC 60695-10-2 | Pass | ||
| 線形膨脹系數(shù) | 流動:-40到40 ℃ | ASTM E831 ISO 11359-2 |
0.00011 | cm/cm/℃ | |
| 流動:23到60 ℃ | ISO 11359-2 | 0.000090 | cm/cm/℃ | ||
| 橫向:-40到40 ℃ | ASTM E831 ISO 11359-2 |
0.00011 | cm/cm/℃ | ||
| 橫向:23到60 ℃ | ISO 11359-2 | 0.000090 | cm/cm/℃ | ||
| 導(dǎo)熱系數(shù) | ISO 8302 | 0.23 | W/m/K | ||
| 電氣性能 | 表面電阻率 | ASTM D257 | ＞1.0E+15 | ohms | |
| 體積電阻率 | ASTM D257 | ＞1.0E+15 | ohm.cm | ||
| 其它 | UL阻燃等級 | 3.00mm | UL 94 | V-2 | |
| 灼熱絲易燃指數(shù) | 1.00mm | IEC 60695-2-12 | 750 | ℃ | |
| 相比耐漏電起痕指數(shù) | (CTI) (PLC) | UL 746 | PLC0 | ||
| 折射率 | ISO 484 | 1.539 | |||
| 透射率 | 2540 µm | ASTM D1003 | 88.0 | % | |
| 霧度 | 2540 µm | ASTM D1003 | 1.0 | % | |