Xyron X0715|(PPE+PS)|Asahi Kasei

流變性能(Rheological properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據
成型收縮(Molding shrinkage) (parallel)	0.6	%	ISO 294-4, 2577
成型收縮(Molding shrinkage) (normal)	0.8	%	ISO 294-4, 2577

機械性能(機械性能(Mechanical properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據
抗拉強度(Tensile Strength)	43	MPa	ISO 527-1/-2
斷裂拉伸應變(Nominal strain at break)	40	%	ISO 527-1/-2
簡支梁缺口沖擊強度(Charpy notched impact strength) (+23°C)	30	kJ/m2	ISO 179/1eA
彎曲彈性模量(Flexural modulus) (23°C)	1920	MPa	ISO 178
ASTM數據(ASTM Data)
抗拉強度(Tensile Strength)	43	MPa	ASTM D 638
斷裂伸長率(Elongation at Break)	70	%	ASTM D 638
彎曲彈性模量(彎曲彈性模量(Flexural Modulus))	1920	MPa	ASTM D 790
抗彎強度(Flexural Strength)	60	MPa	ASTM D 790
懸臂梁式沖擊切口 (1/4 in)	0.282	kJ/m	ASTM D 256

熱性能(熱性能(Thermal properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據
溫度負荷變形(Temp. of deflection under load) (1.80 MPa)	108	°C	ISO 75-1/-2
COEFF線性熱(Coeff. of linear therm. expansion) (parallel)	75	E-6/K	ISO 11359-1/-2
Burning behav. at 1.5 mm nom. thickn.	HB	class	IEC 60695-11-10
厚度測試(Thickness tested)	1.6	mm	IEC 60695-11-10
燃燒性厚度(Burning behav. at thickness h)	HB	class	IEC 60695-11-10
厚度測試(Thickness tested)	3.2	mm	IEC 60695-11-10
ASTM數據(ASTM Data)
UL 94 阻燃等級(Flame rating)	HB	-	UL 94
厚度測試(Thickness tested)	1.6	mm	-
熱膨脹系數(Coefficient of Thermal Expansion) (MD)	75.1	E-6/K	ASTM D 696
DTUL @ 264 psi	113	°C	ASTM D 648

CharacteristicsApplicationsAutomotiveRegional AvailabilityNorth America, Europe, .

轉載請注明: 轉自中國塑膠原料之家 http://www.spnmy.cn/wuxingbiao/

本文鏈接: http://www.spnmy.cn/wuxingbiao/show-102061.html

免責聲明: 本文 Xyron X0715|(PPE+PS)|Asahi Kasei 僅代表作者個人觀點，中國塑膠原料之家無關。中國塑膠原料之家網所轉載的內容，其版權均由原作者和資料提供方所擁有！如因作品版權問題需要處理，請與我們聯絡