SMC 3370 RF ul證書編號:E111031

SMC 3370 RF 物性表: SMC 3370 RF物性表及特性介紹,SMC 3370 RF注塑參數詳情,如需SMC 3370 RF下載, 可到相關下載區下載

品名(產品大類): PPS
阻燃等級(Flame Class): a1
熱絲著火性(HWI): b
高電流電弧著火性 (HAI): b
比較導電徑跡(CTI): b
電氣強度(RTI Elec): r
機械沖擊(RTI Imp): r
機械強度(RTI Str): r
ul證書編號: E111031
UL廠家: POLYNT SPA

UL黃卡查詢 su-jiao.com/ul/	E111031
POLYNT SPA
VIA CADUTI E DISPERSI, DELL'AERONAUTICA 18, BREMBATE DI SOPRABG24030 IT
SMC 3370 RF
Sheet Molding Compound "Polyester" (SMC), furnished as sheets

	Min Thk	Flame			RTI	RTI	RTI
Color	(mm)	Class	HWI	HAI	Elec	Imp	Str
GY	2.0	HB	0	0	130	130	130
	3.6	V-0	0	0	130	130	130

Comparative Tracking Index (CTI):	0	Inclined Plane Tracking (IPT):	-
Dielectric Strength (kV/mm):	-	Volume Resistivity (10x ohm-cm) :	-
High-Voltage Arc Tracking Rate (HVTR):	-	High Volt, Low Current Arc Resis (D495):	-
Dimensional Stability (%):	-

ANSI/UL 94 small-scale test data does not pertain to building materials, furnishings and related contents. ANSI/UL 94 small-scale test data is intended solely for determining the flammability of plastic materials used in the components and parts of end-product devices and appliances, where the acceptability of the combination is determined by UL.

Report Date: 2002-05-24 Last Revised: 2010-06-17

聯系人:趙先生

IEC and ISO Test Methods

			Thickness
Test Name	Test Method	Units	Tested (mm)	Value
Flammability	IEC 60695-11-10	Class (color)	2.0	HB75 (GY)
			3.6	V-0 (GY)
Glow-Wire Flammability (GWFI)	IEC 60695-2-12	C	-	-
Glow-Wire Ignition (GWIT)	IEC 60695-2-13	C	-	-
IEC Comparative Tracking Index	IEC 60112	Volts (Max)	-	-
IEC Ball Pressure	IEC 60695-10-2	C	-	-
ISO Heat Deflection (1.80 MPa)	ISO 75-2	C	-	-
ISO Tensile Strength	ISO 527-2	MPa	-	-
ISO Flexural Strength	ISO 178	MPa	-	-
ISO Tensile Impact	ISO 8256	kJ/m2	-	-
ISO Izod Impact	ISO 180	kJ/m2	-	-
ISO Charpy Impact	ISO 179-2	kJ/m2	-	-

聯系人:趙先生

關鍵詞:
PPS
供應
SMC 3370 RF

轉載請注明: 轉自中國塑膠原料之家 http://www.spnmy.cn/wuxingbiao/

本文鏈接: http://www.spnmy.cn/ul/show-52797.html

免責聲明: 本文 SMC 3370 RF 僅代表作者個人觀點，中國塑膠原料之家無關。中國塑膠原料之家網所轉載的內容，其版權均由原作者和資料提供方所擁有！如因作品版權問題需要處理，請與我們聯絡