E41179 | |
MITSUBISHI ENGINEERING-PLASTICS CORP | |
ENVIRONMENT & QUALITY ASSURANCE DEPT, DIV 1, SHIODOME SUMITOMO-BLDG 25TH FL, 1-9-2 HIGASHI-SHINBASHI, MINATO-KUTOKYO105-0021 JP | |
AN70(+)(f2) | |
Polyphenylene Oxide (PPHOX), "Iupiace", furnished as pellets |
| | Min Thk | Flame | | | RTI | RTI | RTI | | Color | (mm) | Class | HWI | HAI | Elec | Imp | Str | | ALL | 0.75 | V-0 | 1 | 3 | 110 | 105 | 110 | | 1.5 | V-0 | 1 | 3 | 110 | 105 | 110 | | 2.0 | V-0, 5VB | 1 | 3 | 110 | 105 | 110 | | 2.5 | V-0, 5VA | 1 | 3 | 110 | 105 | 110 | | 3.0 | V-0, 5VA | 1 | 3 | 110 | 105 | 110 |
| Comparative Tracking Index (CTI): | 1 | Inclined Plane Tracking (IPT): | 120 min at 1.5kV | | Dielectric Strength (kV/mm): | 32 | Volume Resistivity (10x ohm-cm) : | 16 | | High-Voltage Arc Tracking Rate (HVTR): | 0 | High Volt, Low Current Arc Resis (D495): | 7 | | Dimensional Stability (%): | 0 | | |
| (f2) - | Subjected to one or more of the following tests: Ultraviolet Light, Water Exposure or Immersion in accordance with UL 746C, where the acceptability for outdoor use is to be determined by UL. | | + - | Suffix optional, exceptions: The following cannot be used as optional suffixes: "T" for grade 2030, "A" for 1501, 1502, 1511, 1521 & 2502, "N" for NXG5050, NXG5030, NXG5501, & CGF-(v)(u),"S1" for F20-54. |
| ANSI/UL 94 small-scale test data does not pertain to building materials, furnishings and related contents. ANSI/UL 94 small-scale test data is intended solely for determining the flammability of plastic materials used in the components and parts of end-product devices and appliances, where the acceptability of the combination is determined by UL. |
|
Report Date:
1983-02-10
Last Revised:
2013-08-20 |
郵箱:admin@su-jiao.com |
|
| | | Thickness | | | Test Name | Test Method | Units | Tested (mm) | Value | | Flammability | IEC 60695-11-10, IEC 60695-11-20 | Class (color) | 0.75 | V-0 (ALL) | | | | 1.5 | V-0 (ALL) | | | | 2.0 | V-0, 5VB (ALL) | | | | 2.5 | V-0, 5VA (ALL) | | | | 3.0 | V-0, 5VA (ALL) | | Glow-Wire Flammability (GWFI) | IEC 60695-2-12 | C | - | - | | Glow-Wire Ignition (GWIT) | IEC 60695-2-13 | C | - | - | | IEC Comparative Tracking Index | IEC 60112 | Volts (Max) | - | - | | IEC Ball Pressure | IEC 60695-10-2 | C | - | - | | ISO Heat Deflection (1.80 MPa) | ISO 75-2 | C | - | - | | ISO Tensile Strength | ISO 527-2 | MPa | - | - | | ISO Flexural Strength | ISO 178 | MPa | - | - | | ISO Tensile Impact | ISO 8256 | kJ/m2 | - | - | | ISO Izod Impact | ISO 180 | kJ/m2 | - | - | | ISO Charpy Impact | ISO 179-2 | kJ/m2 | - | - |
|