MPPO-FG15SE ul證書編號:E78964

MPPO-FG15SE 物性表: MPPO-FG15SE物性表及特性介紹,MPPO-FG15SE注塑參數詳情,如需MPPO-FG15SE下載, 可到相關下載區下載

品名(產品大類): PPHOX
阻燃等級(Flame Class): b2
熱絲著火性(HWI): b
高電流電弧著火性 (HAI): e
比較導電徑跡(CTI): f
電氣強度(RTI Elec): b
機械沖擊(RTI Imp): b
機械強度(RTI Str): b
ul證書編號: E78964
UL廠家: MODIFIED PLASTICS INC

中國塑膠原料之家	E78964
MODIFIED PLASTICS INC
1240 E GLENWOOD PL, SANTA ANA CA 92707
MPPO-FG15SE
Polyphenylene Oxide (PPHOX), glass filled, furnished as granular material

	Min Thk	Flame			RTI	RTI	RTI
Color	(mm)	Class	HWI	HAI	Elec	Imp	Str
BK	3.0 ONLY	V-0	0	3	50	50	50

Comparative Tracking Index (CTI):	4	Inclined Plane Tracking (IPT):	-
Dielectric Strength (kV/mm):	-	Volume Resistivity (10x ohm-cm) :	-
High-Voltage Arc Tracking Rate (HVTR):	1	High Volt, Low Current Arc Resis (D495):	7
Dimensional Stability (%):	-

ANSI/UL 94 small-scale test data does not pertain to building materials, furnishings and related contents. ANSI/UL 94 small-scale test data is intended solely for determining the flammability of plastic materials used in the components and parts of end-product devices and appliances, where the acceptability of the combination is determined by UL.

Report Date: 1985-10-02 Last Revised: 2004-10-22

QQ:27660005

IEC and ISO Test Methods

			Thickness
Test Name	Test Method	Units	Tested (mm)	Value
Flammability	IEC 60695-11-10	Class (color)	3.0 ONLY	V-0 (BK)
Glow-Wire Flammability (GWFI)	IEC 60695-2-12	C	-	-
Glow-Wire Ignition (GWIT)	IEC 60695-2-13	C	-	-
IEC Comparative Tracking Index	IEC 60112	Volts (Max)	-	-
IEC Ball Pressure	IEC 60695-10-2	C	-	-
ISO Heat Deflection (1.80 MPa)	ISO 75-2	C	-	-
ISO Tensile Strength	ISO 527-2	MPa	-	-
ISO Flexural Strength	ISO 178	MPa	-	-
ISO Tensile Impact	ISO 8256	kJ/m2	-	-
ISO Izod Impact	ISO 180	kJ/m2	-	-
ISO Charpy Impact	ISO 179-2	kJ/m2	-	-

QQ:27660005

關鍵詞:
供應
PPHOX
MPPO-FG15SE