1900 物性表: 1900物性表及特性介紹,1900注塑參數詳情,如需1900下載, 可到相關下載區下載

品名(產品大類): Acrylic
阻燃等級(Flame Class): b2
熱絲著火性(HWI): a
高電流電弧著火性 (HAI): a
比較導電徑跡(CTI): a
電氣強度(RTI Elec): b
機械沖擊(RTI Imp): b
機械強度(RTI Str): b
ul證書編號: E115252
UL廠家: KYDEX L L C

www.spnmy.cn/ul/	E115252
KYDEX L L C
6685 LOW ST, BLOOMBURG PA 17815
1900
Acrylic/Polyvinylchloride (A/PVC), "KYDEX Product", furnished as sheets

	Min Thk	Flame			RTI	RTI	RTI
Color	(mm)	Class	HWI	HAI	Elec	Imp	Str
ALL	0.70	V-0, 5VB	-	-	50	50	50
	3.0	V-0, 5VA	-	-	50	50	50

Comparative Tracking Index (CTI):	-	Inclined Plane Tracking (IPT):	-
Dielectric Strength (kV/mm):	-	Volume Resistivity (10x ohm-cm) :	-
High-Voltage Arc Tracking Rate (HVTR):	-	High Volt, Low Current Arc Resis (D495):	-
Dimensional Stability (%):	-

ANSI/UL 94 small-scale test data does not pertain to building materials, furnishings and related contents. ANSI/UL 94 small-scale test data is intended solely for determining the flammability of plastic materials used in the components and parts of end-product devices and appliances, where the acceptability of the combination is determined by UL.

Report Date: 2008-07-30 Last Revised: 2013-02-28

郵箱:sales@su-jiao.com

IEC and ISO Test Methods

			Thickness
Test Name	Test Method	Units	Tested (mm)	Value
Flammability	IEC 60695-11-10, IEC 60695-11-20	Class (color)	0.70	V-0, 5VB (ALL)
			3.0	V-0, 5VA (ALL)
Glow-Wire Flammability (GWFI)	IEC 60695-2-12	C	-	-
Glow-Wire Ignition (GWIT)	IEC 60695-2-13	C	-	-
IEC Comparative Tracking Index	IEC 60112	Volts (Max)	-	-
IEC Ball Pressure	IEC 60695-10-2	C	-	-
ISO Heat Deflection (1.80 MPa)	ISO 75-2	C	-	-
ISO Tensile Strength	ISO 527-2	MPa	-	-
ISO Flexural Strength	ISO 178	MPa	-	-
ISO Tensile Impact	ISO 8256	kJ/m2	-	-
ISO Izod Impact	ISO 180	kJ/m2	-	-
ISO Charpy Impact	ISO 179-2	kJ/m2	-	-

郵箱:sales@su-jiao.com

關鍵詞:
供應
1900
Acrylic

轉載請注明: 轉自中國塑膠原料之家 http://www.spnmy.cn/wuxingbiao/

本文鏈接: http://www.spnmy.cn/ul/show-3895.html

免責聲明: 本文 1900 僅代表作者個人觀點，中國塑膠原料之家無關。中國塑膠原料之家網所轉載的內容，其版權均由原作者和資料提供方所擁有！如因作品版權問題需要處理，請與我們聯絡