DIAFOIL N400E ul證書編號:E60476

DIAFOIL N400E 物性表: DIAFOIL N400E物性表及特性介紹,DIAFOIL N400E注塑參數詳情,如需DIAFOIL N400E下載, 可到相關下載區下載

品名(產品大類): Polyethylene
阻燃等級(Flame Class): g7
熱絲著火性(HWI): a
高電流電弧著火性 (HAI): a
比較導電徑跡(CTI): a
電氣強度(RTI Elec): m
機械沖擊(RTI Imp): a
機械強度(RTI Str): m
ul證書編號: E60476
UL廠家: MITSUBISHI PLASTICS INC

UL黃卡查詢 http://www.spnmy.cn/ul/	E60476
MITSUBISHI PLASTICS INC
1-1-1 MARUNOUCHI, CHIYODA-KUTOKYO100-8252 JP
DIAFOIL N400E
Polyethylene Terephthalate (PET), furnished as sheets

	Min Thk	Flame			RTI	RTI	RTI
Color	(mm)	Class	HWI	HAI	Elec	Imp	Str
WT	0.050-0.055	VTM-0	-	-	105	-	105

Comparative Tracking Index (CTI):	-	Inclined Plane Tracking (IPT):	-
Dielectric Strength (kV/mm):	-	Volume Resistivity (10x ohm-cm) :	-
High-Voltage Arc Tracking Rate (HVTR):	-	High Volt, Low Current Arc Resis (D495):	-
Dimensional Stability (%):	-

ANSI/UL 94 small-scale test data does not pertain to building materials, furnishings and related contents. ANSI/UL 94 small-scale test data is intended solely for determining the flammability of plastic materials used in the components and parts of end-product devices and appliances, where the acceptability of the combination is determined by UL.

Report Date: 2013-02-26 Last Revised: 2013-03-15

聯系人:趙經理

IEC and ISO Test Methods

			Thickness
Test Name	Test Method	Units	Tested (mm)	Value
Flammability	ISO 9773	Class (color)	0.050-0.055	VTM-0 (WT)
Glow-Wire Flammability (GWFI)	IEC 60695-2-12	C	-	-
Glow-Wire Ignition (GWIT)	IEC 60695-2-13	C	-	-
IEC Comparative Tracking Index	IEC 60112	Volts (Max)	-	-
IEC Ball Pressure	IEC 60695-10-2	C	-	-
ISO Heat Deflection (1.80 MPa)	ISO 75-2	C	-	-
ISO Tensile Strength	ISO 527-2	MPa	-	-
ISO Flexural Strength	ISO 178	MPa	-	-
ISO Tensile Impact	ISO 8256	kJ/m2	-	-
ISO Izod Impact	ISO 180	kJ/m2	-	-
ISO Charpy Impact	ISO 179-2	kJ/m2	-	-