F660-HA2 WHITE ul證書編號:E86498

F660-HA2 WHITE 物性表: F660-HA2 WHITE物性表及特性介紹,F660-HA2 WHITE注塑參數詳情,如需F660-HA2 WHITE下載, 可到相關下載區下載

品名(產品大類): PA
阻燃等級(Flame Class): d4
熱絲著火性(HWI): a
高電流電弧著火性 (HAI): a
比較導電徑跡(CTI): a
電氣強度(RTI Elec): e
機械沖擊(RTI Imp): e
機械強度(RTI Str): e
ul證書編號: E86498
UL廠家: A L M CORP

中國塑膠原料之家 http://www.spnmy.cn/ul/	E86498
A L M CORP
55 HAUL RD, WAYNE NJ 07470-6612
F660-HA2 WHITE
Polyamide 66 (PA66), furnished as pellets, granular material

	Min Thk	Flame			RTI	RTI	RTI
Color	(mm)	Class	HWI	HAI	Elec	Imp	Str
WT	1.5	V-2	-	-	65	65	65

Comparative Tracking Index (CTI):	-	Inclined Plane Tracking (IPT):	-
Dielectric Strength (kV/mm):	-	Volume Resistivity (10x ohm-cm) :	-
High-Voltage Arc Tracking Rate (HVTR):	-	High Volt, Low Current Arc Resis (D495):	-
Dimensional Stability (%):	-

ANSI/UL 94 small-scale test data does not pertain to building materials, furnishings and related contents. ANSI/UL 94 small-scale test data is intended solely for determining the flammability of plastic materials used in the components and parts of end-product devices and appliances, where the acceptability of the combination is determined by UL.

Report Date: 1992-07-08 Last Revised: 2003-10-24

郵箱:admin@su-jiao.com

IEC and ISO Test Methods

			Thickness
Test Name	Test Method	Units	Tested (mm)	Value
Flammability	IEC 60695-11-10	Class (color)	1.5	V-2 (WT)
Glow-Wire Flammability (GWFI)	IEC 60695-2-12	C	-	-
Glow-Wire Ignition (GWIT)	IEC 60695-2-13	C	-	-
IEC Comparative Tracking Index	IEC 60112	Volts (Max)	-	-
IEC Ball Pressure	IEC 60695-10-2	C	-	-
ISO Heat Deflection (1.80 MPa)	ISO 75-2	C	-	-
ISO Tensile Strength	ISO 527-2	MPa	-	-
ISO Flexural Strength	ISO 178	MPa	-	-
ISO Tensile Impact	ISO 8256	kJ/m2	-	-
ISO Izod Impact	ISO 180	kJ/m2	-	-
ISO Charpy Impact	ISO 179-2	kJ/m2	-	-

郵箱:admin@su-jiao.com

關鍵詞:
PA
供應
F660-HA2 WHITE

轉載請注明: 轉自中國塑膠原料之家 http://www.spnmy.cn/wuxingbiao/

本文鏈接: http://www.spnmy.cn/ul/show-26911.html

免責聲明: 本文 F660-HA2 WHITE 僅代表作者個人觀點，中國塑膠原料之家無關。中國塑膠原料之家網所轉載的內容，其版權均由原作者和資料提供方所擁有！如因作品版權問題需要處理，請與我們聯絡