T383J 物性表: T383J物性表及特性介紹,T383J注塑參數詳情,如需T383J下載, 可到相關下載區下載

品名(產品大類): PF
阻燃等級(Flame Class): b2
熱絲著火性(HWI): b
高電流電弧著火性 (HAI): d
比較導電徑跡(CTI): f
電氣強度(RTI Elec): t
機械沖擊(RTI Imp): t
機械強度(RTI Str): t
ul證書編號: E304813
UL廠家: CHANG CHUN CHEMICAL (ZHANGZHOU) CO LTD

中國塑膠原料之家 www.spnmy.cn/ul/	E304813
CHANG CHUN CHEMICAL (ZHANGZHOU) CO LTD
BAOSHENG RD, LONGCHI INDUSTRY PARK, TAIWANESE INVESTMENT ZONE, ZHANGZHOUFUJIAN363107 CN
T383J
Phenolic Molding Compound (PMC), furnished as pellets or powder

	Min Thk	Flame			RTI	RTI	RTI
Color	(mm)	Class	HWI	HAI	Elec	Imp	Str
BK	6.0-6.6	V-0	0	2	150	150	150

Comparative Tracking Index (CTI):	4	Inclined Plane Tracking (IPT):	-
Dielectric Strength (kV/mm):	-	Volume Resistivity (10x ohm-cm) :	-
High-Voltage Arc Tracking Rate (HVTR):	2	High Volt, Low Current Arc Resis (D495):	6
Dimensional Stability (%):	-

ANSI/UL 94 small-scale test data does not pertain to building materials, furnishings and related contents. ANSI/UL 94 small-scale test data is intended solely for determining the flammability of plastic materials used in the components and parts of end-product devices and appliances, where the acceptability of the combination is determined by UL.

Report Date: 2006-05-22 Last Revised: 2007-12-22

qq:27660005

IEC and ISO Test Methods

			Thickness
Test Name	Test Method	Units	Tested (mm)	Value
Flammability	IEC 60695-11-10	Class (color)	6.0-6.6	V-0 (BK)
Glow-Wire Flammability (GWFI)	IEC 60695-2-12	C	6.0-6.6	960
Glow-Wire Ignition (GWIT)	IEC 60695-2-13	C	6.0-6.6	990
IEC Comparative Tracking Index	IEC 60112	Volts (Max)	-	-
IEC Ball Pressure	IEC 60695-10-2	C	-	-
ISO Heat Deflection (1.80 MPa)	ISO 75-2	C	-	-
ISO Tensile Strength	ISO 527-2	MPa	-	-
ISO Flexural Strength	ISO 178	MPa	-	-
ISO Tensile Impact	ISO 8256	kJ/m2	-	-
ISO Izod Impact	ISO 180	kJ/m2	-	-
ISO Charpy Impact	ISO 179-2	kJ/m2	-	-

qq:27660005

關鍵詞:
供應
PF
T383J

轉載請注明: 轉自中國塑膠原料之家 http://www.spnmy.cn/wuxingbiao/

本文鏈接: http://www.spnmy.cn/ul/show-2052.html

免責聲明: 本文 T383J 僅代表作者個人觀點，中國塑膠原料之家無關。中國塑膠原料之家網所轉載的內容，其版權均由原作者和資料提供方所擁有！如因作品版權問題需要處理，請與我們聯絡