| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.58 g/cc | 0.0571 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.00200 cm/cm | 0.00200 in/in | ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.00700 cm/cm | 0.00700 in/in | ISO 294-4, 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | ISO 527-1/-2 | ||
| Elongation at Break | 2.00 % | 2.00 % | ISO 527-1/-2 | ||
| Tensile Modulus | 10.2 GPa | 1480 ksi | ISO 527-1/-2 | ||
| Flexural Strength | 132 MPa | 19100 psi | ISO 178 | ||
| Flexural Modulus | 9.30 GPa | 1350 ksi | ISO 178 | ||
| Shear Modulus | >= 0.482 GPa @Temperature 200 °C |
>= 69.9 ksi @Temperature 392 °F |
Dynamic; ISO 11403-1,-2 | ||
| >= 0.606 GPa @Temperature 150 °C |
>= 87.9 ksi @Temperature 302 °F |
Dynamic; ISO 11403-1,-2 | |||
| >= 0.983 GPa @Temperature 100 °C |
>= 143 ksi @Temperature 212 °F |
Dynamic; ISO 11403-1,-2 | |||
| >= 2.198 GPa @Temperature 60.0 °C |
>= 318.8 ksi @Temperature 140 °F |
Dynamic; ISO 11403-1,-2 | |||
| >= 2.984 GPa @Temperature 20.0 °C |
>= 432.8 ksi @Temperature 68.0 °F |
Dynamic; ISO 11403-1,-2 | |||
| >= 3.203 GPa @Temperature -10.0 °C |
>= 464.6 ksi @Temperature 14.0 °F |
Dynamic; ISO 11403-1,-2 | |||
| >= 3.701 GPa @Temperature -50.0 °C |
>= 536.8 ksi @Temperature -58.0 °F |
Dynamic; ISO 11403-1,-2 | |||
| Charpy Impact Unnotched | 2.15 J/cm² @Temperature -40.0 °C |
10.2 ft-lb/in² @Temperature -40.0 °F |
ISO 179/1eU | ||
| 2.50 J/cm² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | ||
| 0.400 J/cm² @Temperature -40.0 °C |
1.90 ft-lb/in² @Temperature -40.0 °F |
ISO 179/1eA | |||
| 0.550 J/cm² @Temperature 23.0 °C |
2.62 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 252 °C | 486 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
IEC 60695-11-10 | ||
| HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
IEC 60695-11-10 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | >= 280 °C | >= 536 °F | |||
| 285 °C | 545 °F | Optimum | |||
| <= 300 °C | <= 572 °F | ||||
| Mold Temperature | >= 100 °C | >= 212 °F | |||
| 110 °C | 230 °F | Optimum | |||
| <= 120 °C | <= 248 °F | ||||
| Ejection Temperature | 170 °C | 338 °F | |||
| Drying Temperature | 120 °C @Time 14400 - 21600 sec |
248 °F @Time 4.00 - 6.00 hour |
|||
| Moisture Content | 0.0200 % | 0.0200 % | |||
| Hold Pressure | 80.0 MPa | 11600 psi | |||
| De |
|||||
| Back pressure | As low as possible | ||||
| Drying Recommended | yes | ||||
| Fogging (mg) | 0.1 | G-value (condensate); ISO 6452 | |||
| Hold pressure time | 4 s/mm | ||||
| Max. screw tangential speed (m/s) | 0.2 | ||||
| Part Marking Code | >PET-(MD+GF)35< | ISO 11469 | |||
| Processing | Injection Molding | ||||
| Regional Availability | Asia Pacific | ||||
| Europe | |||||
| Global | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Resin Identification | PET-(MD+GF)35 | ISO 1043 |
|||