| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | Saturation; DIN 53495/1L | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C; 50% RH | ||
| Viscosity Measurement | 108 | 108 | [ml/g]; Viscosity number; ISO 1628 | ||
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | 60x60x2 mm; ISO 294 | ||
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | 60x60x2 mm; ISO 294 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 120 MPa | 17400 psi | 50 mm/min; ISO 527-2 | ||
| Elongation at Break | 3.4 % | 3.4 % | 50mm/min; ISO 527-2 | ||
| Modulus of Elasticity | 8.50 GPa | 1230 ksi | ISO 527-2 | ||
| Charpy Impact Unnotched | 6.00 J/cm² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | ||
| 7.40 J/cm² @Temperature 23.0 °C |
35.2 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 - 225 °C | 428 - 437 °F | DSC; ISO 11357-3 | ||
| Maximum Service Temperature, Air | 210 °C | 410 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-2 | ||
| Decomposition Temperature | >= 290 °C | >= 554 °F | |||
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
|||
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
||||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 °C | 176 °F | Hopper Throat | ||
| Zone 1 | 250 °C | 482 °F | Feeding zone | ||
| Zone 2 | 255 °C | 491 °F | Compression | ||
| Zone 3 | 260 °C | 500 °F | Metering-zone | ||
| Zone 4 | 260 °C | 500 °F | Nozzle | ||
| Melt Temperature | 260 °C | 500 °F | Optimal | ||
| 250 - 280 °C | 482 - 536 °F | Injection-molding | |||
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | Injection molding | ||
| 80.0 °C | 176 °F | Optimal | |||
| Drying Temperature | 80.0 - 120 °C | 176 - 248 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| De |
|||||
| Color | Natural and Black | ||||
| Commercial Status | Europe | ||||
| Ignition Temperature | 350°C | ASTM D1929 | |||
| Peripheral Screw Speed | <0.25 m/s | ||||
| Primary Processing Technique | Injection Molding | ||||