| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | DIN 53495/1L | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50% R.H. | ||
| Viscosity Test | 105 cm³/g | 105 cm³/g | Viscosity number; ISO 1628 | ||
| Linear Mold Shrinkage, Flow | 0.0016 cm/cm | 0.0016 in/in | Sheet | ||
| 0.0043 cm/cm | 0.0043 in/in | 60x60x2mm; ISO 294 | |||
| Linear Mold Shrinkage, Transverse | 0.0074 cm/cm | 0.0074 in/in | 60x60x2mm; ISO 294 | ||
| 0.0082 cm/cm | 0.0082 in/in | Sheet | |||
| Melt Flow | 32.0 g/10 min @Load 2.16 kg, Temperature 275 °C |
32.0 g/10 min @Load 4.76 lb, Temperature 527 °F |
ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 153 MPa | 22200 psi | ISO 2039-1 | ||
| Tensile Strength at Break | 100 MPa | 14500 psi | 5mm/min; ISO 527-2 | ||
| Tensile Strength | 60.0 MPa @Temperature 100 °C |
8700 psi @Temperature 212 °F |
ISO 527 | ||
| 95.0 MPa @Temperature 50.0 °C |
13800 psi @Temperature 122 °F |
ISO 527 | |||
| 120 MPa @Temperature 23.0 °C |
17400 psi @Temperature 73.4 °F |
ISO 527 | |||
| 165 MPa @Temperature -40.0 °C |
23900 psi @Temperature -40.0 °F |
ISO 527 | |||
| Elongation at Break | 2.5 % | 2.5 % | 5mm/min; ISO 527-2 | ||
| Modulus of Elasticity | 6.90 GPa | 1000 ksi | ISO 527-2 | ||
| Flexural Strength | 151 MPa | 21900 psi | ISO 178 | ||
| Charpy Impact Unnotched | 5.50 J/cm² | 26.2 ft-lb/in² | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | ISO 179/1eA | ||
| Dart Drop, Total Energy | <= 5.00 J | <= 3.69 ft-lb | ISO 6603-1 | ||
| Tensile Creep Modulus, 1000 hours | 4700 MPa | 682000 psi | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 2.00e+15 ohm-cm | 2.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 | ||
| Dielectric Constant | 3.6 @Frequency 1.00e+6 Hz |
3.6 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| 3.7 @Frequency 100 Hz |
3.7 @Frequency 100 Hz |
IEC 60250 | |||
| Dielectric Strength | 96.0 kV/mm | 2440 kV/in | IEC 243/1 | ||
| Dissipation Factor | 0.0030 @Frequency 100 Hz |
0.0030 @Frequency 100 Hz |
IEC 60250 | ||
| 0.019 @Frequency 1.00e+6 Hz |
0.019 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Comparative Tracking Index | 125 V | 125 V | Test solution B; IEC 112 | ||
| 450 V | 450 V | Test solution A; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 4.00 µm/m-°C @Temperature 23.0 - 80.0 °C |
2.22 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 53752 | ||
| Specific Heat Capacity | 1.50 J/g-°C | 0.359 BTU/lb-°F | IEC 1006 | ||
| Thermal Conductivity | 0.280 W/m-K | 1.94 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Melting Point | 220 - 225 °C | 428 - 437 °F | ISO 11357-3 | ||
| Maximum Service Temperature, Air | 110 °C | 230 °F | at 50% loss of tensile strength after 20000h; IEC 216-1 | ||
| 140 °C | 284 °F | at 50% loss of tensile strength after 5000h; IEC 216-1 | |||
| 170 °C | 338 °F | ||||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | ISO 75-2 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|||
| HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
||||
| Flame Spread | <= 100 mm/min | <= 3.94 in/min | DIN 75200 | ||
| Glow Wire Test | 760 °C @Thickness 3.00 mm |
1400 °F @Thickness 0.118 in |
IEC 695 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 275 °C | 482 - 527 °F | Injection molding | ||
| 270 °C | 518 °F | for shrinkage test | |||
| Mold Temperature | 80.0 °C | 176 °F | for shrinkage test | ||
| 60.0 - 100 °C | 140 - 212 °F | ||||
| De |
|||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| Light stabilized or stable to light | |||||
| Lubricant | |||||
| U.V. stabilized or stable to weather | |||||
圖：
上海松翰塑化科技有限公司！本公司承諾，假一賠百！所有產品都是原廠家，原包裝一線獨家營銷！
我司所銷售所有產品均為原廠原包，均可提供相關資料報告（如：物性表，MSDS報告，UL報告，COA報告，SGS報告，FDA等）！
歡迎新老客戶來電或QQ咨詢：
聯系人：李先生
聯系電話；13636696005
聯系QQ；1020580970
聯系郵箱；1020580970@qq.com