| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.80 % | 0.80 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50% R.H.; ISO 62 | ||
| Linear Mold Shrinkage | 0.020 cm/cm | 0.020 in/in | ASTM Data; MD | ||
| Linear Mold Shrinkage, Flow | 0.021 cm/cm | 0.021 in/in | ISO Data | ||
| Linear Mold Shrinkage, Transverse | 0.021 cm/cm | 0.021 in/in | ISO Data | ||
| Melt Flow | 2.9 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.9 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 64.0 MPa | 9280 psi | 50mm/min; ISO 527 | ||
| 64.0 MPa | 9280 psi | 2 in/min; ASTM Test | |||
| 33.0 MPa @Temperature 80.0 °C |
4790 psi @Temperature 176 °F |
ISO Data | |||
| Elongation at Break | 30 % | 30 % | 50mm/min, Nominal strain; ISO 527 | ||
| Elongation at Yield | 11 % | 11 % | 50mm/min; ISO 527 | ||
| 11 % | 11 % | 2 in/min; ASTM Test | |||
| 10 % @Temperature 80.0 °C |
10 % @Temperature 176 °F |
ISO Data | |||
| Tensile Modulus | 2.59 GPa | 376 ksi | ASTM Test | ||
| 2.60 GPa | 377 ksi | 1mm/min; ISO 527 | |||
| Flexural Modulus | 2.45 GPa | 355 ksi | ASTM Test | ||
| 2.60 GPa | 377 ksi | ISO Data | |||
| Izod Impact, Notched | 0.694 J/cm @Temperature -40.0 °C |
1.30 ft-lb/in @Temperature -40.0 °F |
ASTM Test | ||
| 0.801 J/cm @Thickness 3.17 mm |
1.50 ft-lb/in @Thickness 0.125 in |
ASTM Test | |||
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | ISO Test | ||
| 5.00 kJ/m² @Temperature -40.0 °C |
2.38 ft-lb/in² @Temperature -40.0 °F |
ISO Test | |||
| Charpy Impact Unnotched | 26.0 J/cm² | 124 ft-lb/in² | ISO 179 | ||
| 20.0 J/cm² @Temperature -30.0 °C |
95.2 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |||
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179 | ||
| 0.550 J/cm² @Temperature -30.0 °C |
2.62 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |||
| Tensile Creep Modulus, 1 hour | 1800 MPa | 261000 psi | ISO 899 | ||
| Tensile Creep Modulus, 1000 hours | 1300 MPa | 189000 psi | ISO 899 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 | ||
| Dielectric Constant | 3.8 @Frequency 100 Hz |
3.8 @Frequency 100 Hz |
IEC 60250 | ||
| 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Dielectric Strength | 40.0 kV/mm | 1020 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0010 @Frequency 100 Hz |
0.0010 @Frequency 100 Hz |
IEC 60250 | ||
| 0.0050 @Frequency 1.00e+6 Hz |
0.0050 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 60.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
33.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM Test | ||
| CTE, linear, Parallel to Flow | 110 µm/m-°C | 61.1 µin/in-°F | ISO 11359 | ||
| Melting Point | 166 °C | 331 °F | 10 K/min | ||
| 166 °C | 331 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 309 °F | ASTM Test | ||
| 156 °C | 313 °F | ISO 75 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ISO 75 | ||
| 96.0 °C | 205 °F | ASTM Test | |||
| Vicat Softening Point | 150 °C | 302 °F | (50 °C/h / 50N) - B/50; ISO 306 | ||
Flammability, UL94  |
HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
|||
| HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
||||
| Oxygen Index | 15 % | 15 % | ISO 4589-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 200 °C | 392 °F | Injection molding | ||
| Mold Temperature | 110 °C | 230 °F | Injection molding | ||
| Injection Velocity | 90.0 mm/sec | 3.54 in/sec | Injection molding | ||
| De |
|||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| FDA | 21 CFR 177.1500 | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| NSF Std. 61 | Yes | ||||
| Primary Processing Technique | Extrusion | ||||
| Processing | Injection Molding | ||||
| Other Extrusion | |||||
| Special characteristic | Release agent | ||||
圖：
上海松翰塑化科技有限公司！本公司承諾，假一賠百！所有產品都是原廠家，原包裝一線獨家營銷！
我司所銷售所有產品均為原廠原包，均可提供相關資料報告（如：物性表，MSDS報告，UL報告，COA報告，SGS報告，FDA等）！
歡迎新老客戶來電或QQ咨詢：
聯系人：李先生
聯系電話；13636696005
聯系QQ；1020580970
聯系郵箱；1020580970@qq.com