| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.650 - 0.900 g/cc | 0.0235 - 0.0325 lb/in³ | |
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 |
| Water Absorption | 0.80 % | 0.80 % | Saturation; ISO 62 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C; 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.017 cm/cm | 0.017 in/in | ISO 2577 |
| Linear Mold Shrinkage, Transverse | 0.019 cm/cm | 0.019 in/in | ISO 2577 |
| Melt Flow | 10.36 g/10 min @Load 2.16 kg, Temperature 190 °C |
10.36 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 145 MPa @Load 36.5 kg, Time 30.0 sec |
21000 psi @Load 80.5 lb, Time 0.00833 hour |
ISO 2039-1 |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527-2 |
| Elongation at Break | 18 % | 18 % | Nominal, 50mm/min; ISO 527-2 |
| Elongation at Yield | 6.5 % | 6.5 % | ISO 527-2 |
| Modulus of Elasticity | 4.00 GPa | 580 ksi | ISO 527-2 |
| Charpy Impact Unnotched | 8.00 J/cm² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 8.50 J/cm² @Temperature 23.0 °C |
40.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.350 J/cm² @Temperature -30.0 °C |
1.67 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.350 J/cm² @Temperature 23.0 °C |
1.67 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 |
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.9 @Frequency 100 Hz |
3.9 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 40.0 kV/mm | 1020 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0050 @Frequency 100 Hz |
0.0050 @Frequency 100 Hz |
IEC 60250 |
| 0.0060 @Frequency 1.00e+6 Hz |
0.0060 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 |
| 600 V | 600 V | Test solution B; IEC 60112 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 131 °F |
DIN 53752 |
| Melting Point | 166 - 186 °C | 331 - 367 °F | |
| Maximum Service Temperature, Air | 100 °C | 212 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | ISO 75-2 |
| Vicat Softening Point | 150 °C | 302 °F | ISO 306 |
| Decomposition Temperature | >= 240 °C | >= 464 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
上海松翰塑化科技有限公司！
本公司承諾，所有產(chǎn)品都是原廠家，原包裝一線獨(dú)家營(yíng)銷！
可提供以下報(bào)告：COA（產(chǎn)地證明）SGS（檢測(cè)報(bào)告）MSDS（成分報(bào)告）FDA（食品安全報(bào)告）UL黃卡（出口報(bào)告）正規(guī)發(fā)票！
歡迎新老客戶來(lái)電咨詢：
聯(lián)系人：夏先生
聯(lián)系電話：135 0180 2636
聯(lián)系 QQ ：205730283
聯(lián)系郵箱：205730283@qq.com