| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.800 g/cc | 0.0289 lb/in³ | ISO 60 |
| Density | 1.64 g/cc | 0.0592 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.40 % | 0.40 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | 60x60x2; 260°C / MT 80°C; 600 bar; ISO 2577 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | 60x60x2; 260°C / MT 80°C; 600 bar; ISO 2577 |
| Melt Flow | 19.68 g/10 min @Load 2.16 kg, Temperature 260 °C |
19.68 g/10 min @Load 4.76 lb, Temperature 500 °F |
ISO 1133-1 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 135 MPa | 19600 psi | at yield, 50 mm/min; ISO 527-1,-2 |
| Elongation at Yield | 2.5 % | 2.5 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 10.0 GPa | 1450 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Strength | 215 MPa | 31200 psi | 2 mm/min; ISO 178-A |
| Flexural Modulus | 10.0 GPa | 1450 ksi | 2 mm/min; ISO 178-A |
| Izod Impact, Notched (ISO) | <= 10.0 kJ/m² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1A |
| <= 10.0 kJ/m² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1U |
| 50.0 kJ/m² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1U | |
| Charpy Impact Unnotched | 5.50 J/cm² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU |
| 5.50 J/cm² @Temperature -30.0 °C |
26.2 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eA |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+17 ohm | 1.00e+17 ohm | IEC 60093 |
| Dielectric Constant | 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.1 @Frequency 100 Hz |
4.1 @Frequency 100 Hz |
IEC 60250 | |
| Dissipation Factor | 0.0030 @Frequency 100 Hz |
0.0030 @Frequency 100 Hz |
IEC 60250 |
| 0.0165 @Frequency 1.00e+6 Hz |
0.0165 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | Solution A; UL 746A |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
11.1 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C @Temperature 23.0 - 55.0 °C |
55.6 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| Melting Point | 222 °C | 432 °F | 10 °C/min; ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-1,-2 |
| Vicat Softening Point | 210 °C | 410 °F | 50 N; 50 °C/h; ISO 306 |
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
|
| V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
||
| V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
||
| Glow Wire Test | 775 °C @Thickness 0.750 mm |
1430 °F @Thickness 0.0295 in |
GWIT; IEC 60695-2-13 |
| 900 °C @Thickness 1.50 mm |
1650 °F @Thickness 0.0591 in |
GWIT; IEC 60695-2-13 | |
| 930 °C @Thickness 3.00 mm |
1710 °F @Thickness 0.118 in |
GWIT; IEC 60695-2-13 | |
| 960 °C @Thickness 0.800 mm |
1760 °F @Thickness 0.0315 in |
GWFI; IEC 60695-2-12 | |
| 960 °C @Thickness 1.50 mm |
1760 °F @Thickness 0.0591 in |
GWFI; IEC 60695-2-12 | |
| 960 °C @Thickness 3.00 mm |
1760 °F @Thickness 0.118 in |
GWFI; IEC 60695-2-12 | |
| Shrinkage | 0.100 % @Temperature 120 °C, Time 14400 sec |
0.100 % @Temperature 248 °F, Time 4.00 hour |
post-shrinkage, 60x60x2; ISO 2577 |
| 0.100 % @Temperature 120 °C, Time 14400 sec |
0.100 % @Temperature 248 °F, Time 4.00 hour |
post-shrinkage, transverse, 60x60x2; ISO 2577 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 250 °C | 482 °F | Injection molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection molding; ISO 294 |
| Dry Time | 4.00 - 8.00 hour @Temperature 120 °C |
4.00 - 8.00 hour @Temperature 248 °F |
|
| Moisture Content | 0.00 - 0.020 % | 0.00 - 0.020 % | Karl Fischer test |