| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | ISO 1183 | ||
| Moisture Absorption | 0.150 % | 0.150 % | 23°C/50%RH; ISO 62 | ||
| Viscosity Test | 80.0 cm³/g | 80.0 cm³/g | ISO 307, 1157, 1628 | ||
| Melt Flow | 10.0 g/10 min @Load 2.16 kg, Temperature 250 °C |
10.0 g/10 min @Load 4.76 lb, Temperature 482 °F |
[cm3/10min]; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 50.0 MPa | 7250 psi | 5mm/min; ISO 527-2/1A | ||
| Elongation at Break | 3.00 % | 3.00 % | 5mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 4.00 GPa | 580 ksi | 50mm/min; ISO 527-2/1A | ||
| Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 | ||
| Charpy Impact Unnotched | 2.20 J/cm² | 10.5 ft-lb/in² | ISO 179/1eU | ||
| 2.30 J/cm² @Temperature -30.0 °C |
10.9 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 0.330 J/cm² | 1.57 ft-lb/in² | ISO 179/1eA | ||
| 0.330 J/cm² @Temperature -30.0 °C |
1.57 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |||
| Tensile Creep Modulus, 1 hour | 3600 MPa | 522000 psi | ISO 899-1 | ||
| Tensile Creep Modulus, 1000 hours | 2500 MPa | 363000 psi | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 4.40 @Frequency 1.00e+6 Hz |
4.40 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| 4.60 @Frequency 100 Hz |
4.60 @Frequency 100 Hz |
IEC 60250 | |||
| Dielectric Strength | 28.0 kV/mm | 711 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.00900 @Frequency 100 Hz |
0.00900 @Frequency 100 Hz |
IEC 60250 | ||
| 0.0120 @Frequency 1.00e+6 Hz |
0.0120 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Comparative Tracking Index | 250 V | 250 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C | 374 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ISO 75-1, -2 | ||
| Vicat Softening Point | 195 °C | 383 °F | ISO 306 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|||
| HB @Thickness 0.820 mm |
HB @Thickness 0.0323 in |
||||
| Oxygen Index | 22.0 % | 22.0 % | ISO 4589 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 75.0 - 100 °C | 167 - 212 °F | cavity | ||
| 260 - 270 °C | 500 - 518 °F | hot runner | |||
| Feed Temperature | 190 - 200 °C | 374 - 392 °F | |||
| Middle Barrel Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| Zone 1 | 250 - 260 °C | 482 - 500 °F | |||
| Zone 2 | 250 - 260 °C | 482 - 500 °F | |||
| Zone 3 | 255 - 265 °C | 491 - 509 °F | |||
| Zone 4 | 255 - 265 °C | 491 - 509 °F | |||
| Die Temperature | 260 - 270 °C | 500 - 518 °F | |||
| Melt Temperature | 260 °C | 500 °F | ISO 294 | ||
| 260 - 270 °C | 500 - 518 °F | ||||
| Mold Temperature | 80.0 °C | 176 °F | ISO 294 | ||
| Injection Velocity | 200 mm/sec | 7.87 in/sec | ISO 294 | ||
| Drying Temperature | 120 - 140 °C | 248 - 284 °F | |||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |||
| Moisture Content | <= 0.0200 % | <= 0.0200 % | |||
| Hold Pressure | 70.0 MPa | 10200 psi | ISO 294 | ||
| Screw Speed | 60.0 rpm @Diameter 55.0 mm |
60.0 rpm @Diameter 2.17 in |
|||
| 75.0 rpm @Diameter 40.0 mm |
75.0 rpm @Diameter 1.57 in |
||||
| 90.0 rpm @Diameter 25.0 mm |
90.0 rpm @Diameter 0.984 in |
||||
| De |
|||||
| Injection molding | Yes | ||||
| Injection speed | fast | ||||
| Processing conditions acc. ISO | 7792 | ||||