LCP ze55311e 材料說明：澤尼特ze55311e是礦物填充具有改進的伸長率的LCP樹脂，低磨損，表面光滑。
LCP ze55311e 性能表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.63 g/cc | 0.0589 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.000500 cm/cm | 0.000500 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00730 cm/cm | 0.00730 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 130 MPa | 18900 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 4.30 % | 4.30 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 8.50 GPa | 1230 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Strength | 140 MPa | 20300 psi | ISO 178 |
| Flexural Modulus | 9.00 GPa | 1310 ksi | ISO 178 |
| Charpy Impact Unnotched | 2.64 J/cm² | 12.6 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 4.27 @Frequency 2.05e+9 Hz |
4.27 @Frequency 2.05e+9 Hz |
|
| Dissipation Factor | 14.0 @Frequency 2.05e+9 Hz |
14.0 @Frequency 2.05e+9 Hz |
|
| Thermal Properties | Metric | English | Comments |
| Melting Point | 320 °C | 608 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 258 °C | 496 °F | ISO 75-1, -2 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|