LCP 5244l 材料說明：澤尼特5244l是40%玻璃/礦物增強改進韌性LCP樹脂。
LCP 5244l 特性：韌性良好
LCP 5244l 的物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.71 g/cc | 0.0618 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00100 cm/cm | 0.00100 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00400 cm/cm | 0.00400 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 131 MPa | 19000 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 1.66 % | 1.66 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 14.0 GPa | 2030 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Strength | 198 MPa | 28700 psi | ISO 178 |
| Flexural Modulus | 13.1 GPa | 1900 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 28.0 kJ/m² @Temperature 23.0 °C |
13.3 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U |
| Charpy Impact Unnotched | 2.70 J/cm² | 12.8 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 1.66 J/cm² | 7.90 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 4.18 @Frequency 2.05e+9 Hz |
4.18 @Frequency 2.05e+9 Hz |
|
| Dissipation Factor | 40.0 @Frequency 2.05e+9 Hz |
40.0 @Frequency 2.05e+9 Hz |
|
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 6.00 µm/m-°C | 3.33 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 48.0 µm/m-°C | 26.7 µin/in-°F | ISO 11359-2 |
| Melting Point | 318 °C | 604 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | ISO 75-1, -2 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|
| V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
||