LCP 5115l 材料說明：澤尼特«5115l是改善韌性注塑15%玻璃纖維增強液晶聚合物。
LCP 5115l 加工方法：注塑成型
LCP 5115l 的物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Linear Mold Shrinkage, Flow | 0.00200 cm/cm | 0.00200 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00900 cm/cm | 0.00900 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 175 MPa | 25400 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 3.00 % | 3.00 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 11.5 GPa | 1670 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Strength | 170 MPa | 24700 psi | ISO 178 |
| Flexural Modulus | 10.5 GPa | 1520 ksi | ISO 178 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 2.50 @Frequency 1.00e+6 Hz |
2.50 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.76 @Frequency 2.05e+9 Hz |
3.76 @Frequency 2.05e+9 Hz |
||
| Dissipation Factor | 0.0159 @Frequency 1.00e+6 Hz |
0.0159 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 30.0 @Frequency 2.05e+9 Hz |
30.0 @Frequency 2.05e+9 Hz |
||
| Thermal Properties | Metric | English | Comments |
| Melting Point | 319 °C | 606 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 275 °C | 527 °F | ISO 75-1, -2 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
|