| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | DAM; ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 36.0 MPa @Temperature 23.0 °C |
5220 psi @Temperature 73.4 °F |
DAM; ISO 527 | ||
| Elongation at Break | >= 50 % @Temperature 23.0 °C |
>= 50 % @Temperature 73.4 °F |
DAM; nominal; ISO 527 | ||
| 170 % @Temperature 23.0 °C |
170 % @Temperature 73.4 °F |
DAM; nominal; ISO 527 | |||
| 200 % @Temperature 23.0 °C |
200 % @Temperature 73.4 °F |
DAM; ISO 527 | |||
| Tensile Modulus | 0.930 GPa @Temperature 23.0 °C |
135 ksi @Temperature 73.4 °F |
DAM; ISO 527 | ||
| Flexural Modulus | 0.980 GPa @Temperature 23.0 °C |
142 ksi @Temperature 73.4 °F |
DAM; ISO 178 | ||
| Izod Impact, Notched (ISO) | 25.0 kJ/m² @Temperature -40.0 °C |
11.9 ft-lb/in² @Temperature -40.0 °F |
DAM; ISO 180/1A | ||
| 60.0 kJ/m² @Temperature -20.0 °C |
28.6 ft-lb/in² @Temperature -4.00 °F |
DAM; ISO 180/1A | |||
| 95.0 kJ/m² @Temperature 23.0 °C |
45.2 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 180/1A | |||
| Charpy Impact, Notched | 3.00 J/cm² @Temperature -40.0 °C |
14.3 ft-lb/in² @Temperature -40.0 °F |
DAM; ISO 179/1eA | ||
| 10.5 J/cm² @Temperature 23.0 °C |
50.0 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 263 °C | 505 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | DAM; ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 285 °C | 545 °F | DAM; Optimum; Injection Molding | ||
| 275 - 295 °C | 527 - 563 °F | DAM; Injection Molding | |||
| Mold Temperature | 60.0 °C | 140 °F | DAM; optimum; Injection Molding | ||
| 40.0 - 80.0 °C | 104 - 176 °F | DAM; Injection Molding | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM; Injection Molding | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM; Injection Molding | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM; Injection Molding | ||
| De |
|||||
| Appearance | Black Color | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA66-F< | ISO 11469; DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Extrusion Resins | DAM | |||
| Toughened Resins | DAM | ||||
| Unreinforced Resins | DAM | ||||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA66-F | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
概述
PA塑料(尼龍，聚酰胺)，英文名稱:Polyamide
PA的品種繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近幾年開發的半芳香族尼龍PA6T和特種尼龍等很多新品種。
物理性能
比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米
成型收縮率：PA6 0.8-2.5% ，PA66 1.5-2.2%
成型溫度：220-300℃
干燥條件：100-110℃/12小時
堅韌、耐磨、耐油、,耐水、抗酶菌、但吸水大
燃燒鑒別方法：火焰上端黃色，下端藍色，燃燒后塑料熔滴落，起泡，離火后特殊的羊毛，指甲燒焦味和帶芹菜味
|
尼龍6： |
彈性好，沖擊強度，吸水較大 |
|
尼龍66： |
性能優于尼龍6，強度高，耐磨性好 |
|
尼龍610： |
與尼龍66相似，但吸水小，剛度低 |
|
尼龍1010： |
半透明，吸水小。耐寒性較好。適于制作一般機械零件、減磨耐磨零件、傳動零件以及化工、電器、儀表等零件 |
成型性能
1、結晶料，熔點較高，熔融溫度范圍窄，熱穩定性差，料溫超過300度、滯留時間超過30分鐘即分解。較易吸濕，需干燥，含水量不得超過0.3%。
2、流動性好，易溢料。宜用自鎖時噴嘴，并應加熱。
3、成型收縮范圍及收縮率大，方向性明顯，易發生縮孔、變形等。
4、模溫按塑件壁厚在20～90度范圍內選取，注射壓力按注射機類型、料溫、塑件形狀尺寸、模具澆注系統選定，成型周期按塑件壁厚選定。樹脂粘度小時，注射、冷卻時間應取長，并用白油作脫模劑。
5、模具澆注系統的形式和尺寸，增大流道和澆口尺寸可減少縮水。
聚酰胺的不足之處在于：由于熱膨脹和吸水性所至的尺寸精度不夠，耐酸性差，硬度和彈性模量不夠。經改良以后，也是比較優秀的工程塑料之一。
應用
汽車制造方面
用于制造燃料濾網、燃料過濾器、罐、捕集器、儲油槽、發動機汽缸蓋罩、散熱器水缸、平衡旋轉軸齒輪。也可用在汽車的電器配件、接線柱等。另外，它還可用作驅動、控制部件等。
電器電子工業
可用于制造電飯鍋、電動吸塵器、高頻電子食品加熱器，電器產品的接線柱、開關和電阻器等。
醫療器械儀器
用于醫用輸血管、取血器、輸液器等。PA單絲可做外科手術縫線、假發等；另外，電子打字機的數字旋轉盤、接線柱、傳動齒輪、印刷機的帶式過濾片等。
其它方面
用于制作一次性打火機體、堿性干電池襯墊，摩托車駕駛員的頭盔，辦公機器外殼，辦公用椅的角輪、座和靠背，冰鞋、釣魚線等，PA薄膜氣體阻隔性能優良，而且耐油性、耐低溫沖擊性、耐穿透性好，可用于肉、火腿腸等冷凍食品的包裝。聚酰胺還可棒材和板材，也作齒輪或其它傳動裝置。
上海浩銘塑膠有限公司！本公司承諾，所有產品都是原廠家，原包裝一線獨家營銷！
可提供以下報告：COA（產地證明）SGS（檢測報告）MSDS（成分報告）FDA（食品安全報告）UL黃卡（出口報告）正規發票！歡迎新老客戶來電咨詢：
聯系人：鄧小姐
聯系電話：13917657923
聯系QQ:996152797
聯系郵箱：996152797@qq.com