| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ASTM D792 |
| 1.28 g/cc | 0.0462 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| 0.250 % | 0.250 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm @Time 86400 sec |
0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0072 cm/cm @Time 86400 sec |
0.0072 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0078 cm/cm @Time 86400 sec |
0.0078 in/in @Time 24.0 hour |
ISO 294 |
| 0.0080 cm/cm @Time 86400 sec |
0.0080 in/in @Time 24.0 hour |
ASTM D955 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 88.0 MPa | 12800 psi | ASTM D638 |
| 98.0 MPa | 14200 psi | ISO 527 | |
| Tensile Strength, Yield | 105 MPa | 15200 psi | ASTM D638 |
| 106 MPa | 15400 psi | ISO 527 | |
| Elongation at Break | 9.7 % | 9.7 % | ISO 527 |
| 27.5 % | 27.5 % | ASTM D638 | |
| Elongation at Yield | 6.8 % | 6.8 % | ISO 527 |
| 7.0 % | 7.0 % | ASTM D638 | |
| Tensile Modulus | 3.18 GPa | 461 ksi | 1 mm/min; ISO 527 |
| 3.33 GPa | 483 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 112 MPa | 16200 psi | ISO 178 |
| 151 MPa | 21900 psi | ASTM D790 | |
| Flexural Modulus | 3.14 GPa | 455 ksi | ISO 178 |
| 3.48 GPa | 505 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 13.77 J/cm | 25.80 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 89.0 kJ/m² | 42.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J | 4.43 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.43 | 0.43 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.45 | 0.45 | ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 43.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
24.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 43.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
24.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 41.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 41.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 187 °C | 369 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 190 °C @Thickness 3.20 mm |
374 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
上海松翰塑化科技有限公司，供應原料，品質真實,物實價廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
歡迎各位客戶前來咨詢：
聯系人： 夏先生
手 機：13501802636 021 51131842
QQ ：205730283
郵 箱 ：205730283@qq.com
PEI EX03599H 圖：