| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.58 g/cc | 0.0571 lb/in³ | ASTM D 792 |
| 1.58 g/cc | 0.0571 lb/in³ | ISO 1183 | |
| Moisture Absorption at Equilibrium | 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0069 cm/cm @Time 86400 sec |
0.0069 in/in @Time 24.0 hour |
ISO 294 |
| 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D 955 | |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.012 cm/cm @Time 86400 sec |
0.010 - 0.012 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.011 cm/cm @Time 86400 sec |
0.011 in/in @Time 24.0 hour |
ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 117 MPa | 17000 psi | ASTM D 638 |
| 117 MPa | 17000 psi | ISO 527 | |
| Tensile Strength, Yield | 117 MPa | 17000 psi | ASTM D 638 |
| 117 MPa | 17000 psi | ISO 527 | |
| Elongation at Break | 1.4 % | 1.4 % | ASTM D 638 |
| 1.4 % | 1.4 % | ISO 527 | |
| Elongation at Yield | 1.4 % | 1.4 % | ASTM D 638 |
| 1.4 % | 1.4 % | ISO 527 | |
| Tensile Modulus | 17.32 GPa | 2512 ksi | 1 mm/min; ISO 527 |
| 20.68 GPa | 2999 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 179 MPa | 26000 psi | ASTM D 790 |
| 179 MPa | 26000 psi | ISO 178 | |
| Flexural Modulus | 16.54 GPa | 2399 ksi | ASTM D 790 |
| 17.3 GPa | 2510 ksi | ISO 178 | |
| Izod Impact, Notched | 0.480 J/cm @Temperature 23.0 °C |
0.899 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 4.80 J/cm @Temperature 23.0 °C |
8.99 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 27.0 kJ/m² @Temperature 23.0 °C |
12.8 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| 9.00 J @Temperature 23.0 °C |
6.64 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 | |
| Coefficient of Friction, Dynamic | 0.38 | 0.38 | ASTM D 3702 Modified |
| Coefficient of Friction, Static | 0.31 | 0.31 | ASTM D 3702 Modified |
| K (wear) Factor | 127 x 10-8 mm³/N-M | 63.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D 3702 Modified |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 43.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 43.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
24.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 27.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
15.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 27.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
15.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 163 °C | 325 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 162 °C @Thickness 3.20 mm |
324 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 159 °C | 318 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 160 °C @Thickness 3.20 mm |
320 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
上海松翰塑化科技有限公司，供應原料，品質(zhì)真實,物實價廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
歡迎各位客戶前來咨詢：
聯(lián)系人： 夏先生
手 機：13501802636 021 51131842
QQ ：205730283
郵 箱 ：205730283@qq.com
POM-KCL36 圖：