| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.80 % | 0.80 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C; 50% RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.021 cm/cm | 0.021 in/in | ISO 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.021 cm/cm | 0.021 in/in | ISO 2577 | ||
| Melt Flow | 13 g/10 min @Load 2.16 kg, Temperature 190 °C |
13 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 145 MPa @Load 36.5 kg, Time 30.0 sec |
21000 psi @Load 80.5 lb, Time 0.00833 hour |
ISO 2039-1 | ||
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | 50 mm/min; ISO 527-2 | ||
| Elongation at Break | 28 % | 28 % | ISO 527-2 | ||
| Elongation at Yield | 9.0 % | 9.0 % | ISO 527-1/-2 | ||
| Modulus of Elasticity | 2.70 GPa | 392 ksi | ISO 527-2 | ||
| Izod Impact, Notched (ISO) | 5.50 kJ/m² @Temperature -30.0 °C |
2.62 ft-lb/in² @Temperature -22.0 °F |
ISO 180/A | ||
| 5.50 kJ/m² @Temperature 23.0 °C |
2.62 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A | |||
| Charpy Impact Unnotched | 17.0 J/cm² @Temperature -30.0 °C |
80.9 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | ||
| 18.0 J/cm² @Temperature 23.0 °C |
85.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 0.500 J/cm² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | ||
| 0.550 J/cm² @Temperature 23.0 °C |
2.62 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |||
| Tensile Creep Modulus, 1000 hours | 1300 MPa | 189000 psi | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 | ||
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| 3.8 @Frequency 100 Hz |
3.8 @Frequency 100 Hz |
IEC 60250 | |||
| Dielectric Strength | 40.0 kV/mm | 1020 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0010 @Frequency 100 Hz |
0.0010 @Frequency 100 Hz |
IEC 60250 | ||
| 0.0050 @Frequency 1.00e+6 Hz |
0.0050 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 | ||
| 600 V | 600 V | Test solution B; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 11.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
6.11 µin/in-°F @Temperature 73.4 - 131 °F |
DIN 53752 | ||
| Melting Point | 167 °C | 333 °F | |||
| Maximum Service Temperature, Air | 100 °C | 212 °F | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ISO 75-2 | ||
| Vicat Softening Point | 150 °C | 302 °F | ISO 306 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 190 - 230 °C | 374 - 446 °F | Injection-molding | ||
| Mold Temperature | 60.0 - 120 °C | 140 - 248 °F | |||
| Drying Temperature | 100 °C | 212 °F | |||
| Dry Time | 3 hour | 3 hour | |||
| De |
|||||
| Color | BK 00120 | ||||
| Commercial Status | Europe | ||||
| Primary Processing Technique | Injection Molding | ||||
POM 的簡介
聚甲醛學名聚氧化聚甲醛（簡稱POM） 又稱賽鋼、特鋼。
它是以甲醛等為原料聚合所得。
POM-H（聚甲醛均聚物），POM-K（聚甲醛共聚物）是高密度、高結晶度的熱塑性工程塑料。
具有良好的物理、機械和化學性能，尤其是有優異的耐摩擦性能。
POM具有較好的綜合性能，在熱塑性塑料中是最堅硬的，是塑料材料中力學性能最接近金屬的品種之一，其抗張強度、彎曲強度、耐疲勞強度，耐磨性和電性都十分優良，可在-40度--100度之間長期使用。
POM 電學性能
POM的電絕緣性較好，幾乎不受溫度和濕度的影響；介電常數和介電損耗在很寬的溫度、濕度和頻率范圍內變化很小；耐電弧性極好，并可在高溫下保持。POM的介電強度與厚度有關，厚度0.127mm時為82.7kV/mm，厚度為1.88mm時為23.6kV/mm。
POM具有很低的摩擦系數和很好的幾何穩定性，特別適合于制作齒輪和軸承。由于它還具有耐高溫特性，因此還用于管道器件（管道閥門、泵殼體），草坪設備等。
POM 環境性能:
POM不耐強酸和氧化劑，對烯酸及弱酸有一定的穩定性。
POM的耐溶劑性良好，可耐烴類、醇類、醛類、醚類、汽油、潤滑油及弱堿等，并可在高溫下保持相當的化學穩定性。吸水性小，尺寸穩定性好。
POM的耐候性不好，長期在紫外線作用下，力學性能下降，表面發生粉化和龜裂。
應用范圍：
POM屬結晶性塑料，熔點明顯，一旦達到熔點，熔體粘度迅速下降。當溫度超過一定限度或熔體受熱時間過長，會引起分解。
POM具有較好的綜合性能，在熱塑性塑料中是最堅硬的，是塑料材料中力學性能最接近金屬的品種之一，其抗張強度、彎曲強度、耐疲勞強度，耐磨性和電性都十分優良，可在-40度--100度之間長期使用。
上海松翰塑化科技有限公司，供應原料，品質真實,物實價廉。