| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.850 g/cc | 0.0307 lb/in³ | |||
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.80 % | 0.80 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C; 50% RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.021 cm/cm | 0.021 in/in | ISO 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.021 cm/cm | 0.021 in/in | ISO 2577 | ||
| Melt Flow | 15.4 g/10 min @Load 2.16 kg, Temperature 190 °C |
15.4 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 130 MPa @Load 36.5 kg, Time 30.0 sec |
18900 psi @Load 80.5 lb, Time 0.00833 hour |
ISO 2039-1 | ||
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527-2 | ||
| Elongation at Break | 32 % | 32 % | ISO 527-2 | ||
| Elongation at Yield | 11 % | 11 % | ISO 527-2 | ||
| Modulus of Elasticity | 2.45 GPa | 355 ksi | ISO 527-2 | ||
| Charpy Impact Unnotched | 21.0 J/cm² @Temperature -30.0 °C |
99.9 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | ||
| 25.0 J/cm² @Temperature 23.0 °C |
119 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | ||
| 0.650 J/cm² @Temperature 23.0 °C |
3.09 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |||
| Tensile Creep Modulus, 1000 hours | 1000 MPa | 145000 psi | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| 3.9 @Frequency 100 Hz |
3.9 @Frequency 100 Hz |
IEC 60250 | |||
| Dielectric Strength | 36.0 kV/mm | 914 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0030 @Frequency 100 Hz |
0.0030 @Frequency 100 Hz |
IEC 60250 | ||
| 0.0060 @Frequency 1.00e+6 Hz |
0.0060 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 | ||
| 600 V | 600 V | Test solution B; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 110 µm/m-°C @Temperature 23.0 - 55.0 °C |
61.1 µin/in-°F @Temperature 73.4 - 131 °F |
DIN 53752 | ||
| Melting Point | 167 °C | 333 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 100 °C | 212 °F | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ISO 75-2 | ||
| Vicat Softening Point | 150 °C | 302 °F | ISO 306 | ||
| Decomposition Temperature | >= 240 °C | >= 464 °F | |||
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 200 °C | 392 °F | Hopper Throat | ||
| Zone 1 | 200 °C | 392 °F | Feed zone | ||
| Zone 2 | 200 °C | 392 °F | Compression | ||
| Zone 3 | 200 °C | 392 °F | Metering-zone | ||
| Zone 4 | 200 °C | 392 °F | Nozzle | ||
| Melt Temperature | 200 °C | 392 °F | Optimal | ||
| 190 - 230 °C | 374 - 446 °F | Injection-molding | |||
| Mold Temperature | 60.0 - 120 °C | 140 - 248 °F | Injection-molding | ||
| 90.0 °C | 194 °F | Optimal | |||
| Drying Temperature | 100 °C | 212 °F | |||
| Dry Time | 3 hour | 3 hour | |||
| De |
|||||
| Commercial Status | Europe | ||||
| Ignition Temperature | 320 - 340°C | ASTM D1929 | |||
| Peripheral Screw Speed | <0.3 m/s | ||||
| Primary Processing Technique | Injection Molding | ||||
POM 的簡(jiǎn)介
聚甲醛學(xué)名聚氧化聚甲醛（簡(jiǎn)稱POM） 又稱賽鋼、特鋼。
它是以甲醛等為原料聚合所得。
POM-H（聚甲醛均聚物），POM-K（聚甲醛共聚物）是高密度、高結(jié)晶度的熱塑性工程塑料。
具有良好的物理、機(jī)械和化學(xué)性能，尤其是有優(yōu)異的耐摩擦性能。
POM具有較好的綜合性能，在熱塑性塑料中是最堅(jiān)硬的，是塑料材料中力學(xué)性能最接近金屬的品種之一，其抗張強(qiáng)度、彎曲強(qiáng)度、耐疲勞強(qiáng)度，耐磨性和電性都十分優(yōu)良，可在-40度--100度之間長(zhǎng)期使用。
POM 電學(xué)性能
POM的電絕緣性較好，幾乎不受溫度和濕度的影響；介電常數(shù)和介電損耗在很寬的溫度、濕度和頻率范圍內(nèi)變化很小；耐電弧性極好，并可在高溫下保持。POM的介電強(qiáng)度與厚度有關(guān)，厚度0.127mm時(shí)為82.7kV/mm，厚度為1.88mm時(shí)為23.6kV/mm。
POM具有很低的摩擦系數(shù)和很好的幾何穩(wěn)定性，特別適合于制作齒輪和軸承。由于它還具有耐高溫特性，因此還用于管道器件（管道閥門、泵殼體），草坪設(shè)備等。
POM 環(huán)境性能:
POM不耐強(qiáng)酸和氧化劑，對(duì)烯酸及弱酸有一定的穩(wěn)定性。
POM的耐溶劑性良好，可耐烴類、醇類、醛類、醚類、汽油、潤滑油及弱堿等，并可在高溫下保持相當(dāng)?shù)幕瘜W(xué)穩(wěn)定性。吸水性小，尺寸穩(wěn)定性好。
POM的耐候性不好，長(zhǎng)期在紫外線作用下，力學(xué)性能下降，表面發(fā)生粉化和龜裂。
應(yīng)用范圍：
POM屬結(jié)晶性塑料，熔點(diǎn)明顯，一旦達(dá)到熔點(diǎn)，熔體粘度迅速下降。當(dāng)溫度超過一定限度或熔體受熱時(shí)間過長(zhǎng)，會(huì)引起分解。
POM具有較好的綜合性能，在熱塑性塑料中是最堅(jiān)硬的，是塑料材料中力學(xué)性能最接近金屬的品種之一，其抗張強(qiáng)度、彎曲強(qiáng)度、耐疲勞強(qiáng)度，耐磨性和電性都十分優(yōu)良，可在-40度--100度之間長(zhǎng)期使用。
上海松翰塑化科技有限公司，供應(yīng)原料，品質(zhì)真實(shí),物實(shí)價(jià)廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
歡迎各位客戶前來咨詢：
聯(lián)系人： 夏先生
手 機(jī)：13501802636
QQ ：205730283
郵 箱 ：205730283@qq.com
參考圖如下：