TPU 5080A 物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 80 | 80 | ASTM D2240 |
| Tensile Strength at Break | 33.0 MPa | 4790 psi | ASTM D412 |
| Tensile Stress | 4.00 MPa @Strain 100 % |
580 psi @Strain 100 % |
ASTM D412 |
| 13.0 MPa @Strain 300 % |
1890 psi @Strain 300 % |
ASTM D412 | |
| Elongation at Break | 680 % | 680 % | ASTM D412 |
| Tear Strength | 550 kN/m | 3140 pli | Die C; ASTM D412 |
| Taber Abrasion, mg/1000 Cycles | 24 | 24 | ASTM D1044 |
| Abrasion | 25 | 25 | mm3; DIN 53516 |
| Compression Set | 18 % @Temperature 22.8 °C, Time 79200 sec |
18 % @Temperature 73.0 °F, Time 22.0 hour |
ASTM D3995B |
| 32 % @Temperature 70.0 °C, Time 259000 sec |
32 % @Temperature 158 °F, Time 72.0 hour |
ASTM D3995B | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 82.2 °C | 180 °F | ASTM D1525 |
| Brittleness Temperature | -37.0 °C | -34.6 °F | ASTM D746 |
| Flammability, UL94 | HB @Thickness 1.00 mm |
HB @Thickness 0.0394 in |
|
| HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
||
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
||
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 200 - 205 °C | 392 - 401 °F | Injection |
| 205 °C | 401 °F | Gate Temperature; Extrusion | |
| Rear Barrel Temperature | 175 °C | 347 °F | Injection |
| Middle Barrel Temperature | 190 °C | 374 °F | Injection |
| Front Barrel Temperature | 205 °C | 401 °F | Injection |
| Nozzle Temperature | 205 - 210 °C | 401 - 410 °F | Injection |
| Zone 1 | 175 °C | 347 °F | Extrusion |
| Zone 2 | 190 °C | 374 °F | Extrusion |
| Zone 3 | 205 °C | 401 °F | Extrusion |
| Die Temperature | 210 °C | 410 °F | Extrusion |
| Mold Temperature | 25.0 - 60.0 °C | 77.0 - 140 °F | Injection |
| Injection Velocity | >= 10.0 mm/sec | >= 0.394 in/sec | Injection |
| Drying Temperature | 85.0 °C | 185 °F | Injection |
| 85.0 °C | 185 °F | Extrusion | |
| Dry Time | 4.00 hour | 4.00 hour | Injection |
| 4.00 hour | 4.00 hour | Extrusion | |
| Back Pressure | 0.500 - 1.00 MPa | 72.5 - 145 psi | Injection |
| Clamp Pressure | 40.0 - 70.3 MPa | 5800 - 10200 psi | Injection |
| Screw Speed | 60 - 200 rpm | 60 - 200 rpm | Injection |
應用介紹
1．薄膜和片材（TPU具較好耐磨性、抗刺穿性、抗撕裂性、彈性、粘合性）（TPU薄膜應用在冬季服裝、鞋類具有防寒、保暖、防水性能好等特性外還具有特別好的透氣性）
2．管材（TPU具有高伸長率，良好耐水解和抗微生物性、耐油性、優異機械性能，如作消防水管內襯，輸y油管氣動軟管等）
3．鞋底，鞋邦等鞋材料（TPU具有突出耐磨性、抗刮性、耐刺穿性、抗縱向彎曲強度和低溫沖擊強度，其耐撕裂性和抗裂紋傳播性是所有塑料中最好的。如作溜冰、滑雪靴、運動鞋、特種功能鞋等）
4．電線、電纜、光纜護套（TPU具良好耐磨性、耐環境、耐候性、耐腐蝕性、絕緣性、彈性和低溫柔韌性等）
5．拉鏈片、高檔塑料表帶、表殼以及潛水表、禮品表等系列（TPU具有高彈、耐折、耐水性好手感舒適等）
6．機械制品和其它應用（如制造汽車部件、機械軸承、滾輪、輸送帶、橡塑篩網、工業膠管,墊圈,密封圈,游泳鏡,沖浪板,表帶,動物標牌,電器零部件,涂料,粘合劑,纖維等.) 上海松翰塑化科技有限公司供應產品，品質一流，TPV種類齊全。 公司理念你的要求就是我們的追求 。咨詢人夏先生 電話：13751253137 QQ：205730283 我公司將給你最專業產品加工工藝指導及幫你解決加工工藝難題 歡迎你的咨詢