| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.53 g/cc | 1.53 g/cc | ISO 1183 | ||
| Melt Flow | 13 g/10 min @Load 2.16 kg, Temperature 250 °C |
13 g/10 min @Load 4.76 lb, Temperature 482 °F |
ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 123 MPa | 17800 psi | ISO 527-2/1 | ||
| Elongation at Break | 3.1 % | 3.1 % | ISO 527-2/1 | ||
| Tensile Modulus | 9.01 GPa | 1310 ksi | ISO 527-2/1A | ||
| Flexural Strength | 189 MPa | 27400 psi | ISO 178 | ||
| Flexural Modulus | 9.25 GPa | 1340 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 7.50 kJ/m² | 3.57 ft-lb/in² | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 396 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|||
| Processing Properties | Metric | English | Comments | ||
| Nozzle Temperature | 240 - 260 °C | 464 - 500 °F | |||
| Melt Temperature | 230 - 260 °C | 446 - 500 °F | |||
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |||
| Drying Temperature | 120 - 140 °C | 248 - 284 °F | |||
| Dry Time | 3 - 4 hour | 3 - 4 hour | |||
| Back Pressure | 0.300 - 0.700 MPa | 43.5 - 102 psi | |||
| De |
|||||
| Processing Screw Speed | Medium-Fast | ||||