顆粒圖：
、
、物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | ASTM D792 |
| Water Absorption | 0.030 % @Time 86400 sec |
0.030 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage | 0.0075 - 0.010 cm/cm | 0.0075 - 0.010 in/in | ASTM D955 |
| Melt Flow | 15 g/10 min @Load 3.80 kg, Temperature 250 °C |
15 g/10 min @Load 8.38 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 53.0 MPa @Thickness 3.17 mm |
7690 psi @Thickness 0.125 in |
ASTM D638 |
| Elongation at Break | 115 % @Thickness 3.17 mm |
115 % @Thickness 0.125 in |
ASTM D638 |
| Flexural Strength | 82.0 MPa @Thickness 3.17 mm |
11900 psi @Thickness 0.125 in |
ASTM D790 |
| Flexural Modulus | 2.00 GPa @Thickness 3.17 mm |
290 ksi @Thickness 0.125 in |
ASTM D790 |
| Izod Impact, Notched | 5.34 J/cm @Temperature -20.0 °C |
10.0 ft-lb/in @Temperature -4.00 °F |
ASTM D256 |
| 8.01 J/cm @Thickness 3.17 mm |
15.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 101 °C | 214 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 °C | 210 °F | ASTM D648 |
| UL RTI, Electrical | 75.0 °C | 167 °F | |
| UL RTI, Mechanical with Impact | 75.0 °C | 167 °F | |
| UL RTI, Mechanical without Impact | 75.0 °C | 167 °F | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
|
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
||
上海松翰塑化科技有限公司，供應(yīng)原料，品質(zhì)真實(shí),物實(shí)價(jià)廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
歡迎各位客戶前來咨詢：
聯(lián)系人： 夏先生
手 機(jī)：13501802636
QQ ：205730283
郵 箱 ：205730283@qq.com