PA66 G5 FR C4 25%玻璃纖維增強，阻燃、

PA66 G5 FR C4 塑膠原料為半透明或不透明乳白包或帶黃色顆粒狀結(jié)晶形聚合物，具有可塑性。密度（g/cm3） 1．10-1．14；拉伸強度(MPa) 60. 0-80．0；洛氏硬度118；熔點252℃；脆化溫度-30℃；熱分解溫度大于350℃；連續(xù)耐熱80-120℃；沖擊強度（kJ/m2） 60-100；靜彎曲強度(MPa) 1 00-120；馬丁耐熱(℃) 50-60；彎曲彈性模量 (MPa) 2000～3000；體積電阻率（Ωcm） 1.83×1015；平衡吸水率2．5%；介電常數(shù) 1．63。

Physical Properties	Metric	English	Comments
Density	1.58 g/cc	0.0571 lb/in³	ASTM D792, ISO 1183
Water Absorption	0.50 %	0.50 %	23°C, 24h in H2O; sim. ISO 62
Water Absorption at Saturation	4.0 %	4.0 %	sim. ISO 62
Linear Mold Shrinkage, Flow	0.0040 cm/cm	0.0040 in/in	parallel; Euronil
Linear Mold Shrinkage, Transverse	0.0070 cm/cm	0.0070 in/in	Euronil
Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	125 MPa	18100 psi	ISO 527, ASTM D638
Elongation at Break	2.0 %	2.0 %
Tensile Modulus	8.00 GPa	1160 ksi	ISO 527, ASTM D638
Flexural Yield Strength	185 MPa	26800 psi	ISO 178, ASTM D790
	130 MPa @Temperature 90.0 °C	18900 psi @Temperature 194 °F	ISO 178, ASTM D790
Flexural Modulus	8.50 GPa	1230 ksi	ISO 178, ASTM D790
	4.80 GPa @Temperature 90.0 °C	696 ksi @Temperature 194 °F	ISO 178, ASTM D790
Izod Impact, Notched (ISO)	5.00 kJ/m² @Temperature -30.0 °C	2.38 ft-lb/in² @Temperature -22.0 °F	ISO 180/1A
	6.50 kJ/m² @Temperature 23.0 °C	3.09 ft-lb/in² @Temperature 73.4 °F	ISO 180/1A
Charpy Impact Unnotched	2.70 J/cm²	12.8 ft-lb/in²	ISO 179
	2.40 J/cm² @Temperature -30.0 °C	11.4 ft-lb/in² @Temperature -22.0 °F	ISO 179
Charpy Impact, Notched	0.600 J/cm²	2.86 ft-lb/in²	ISO 179
	0.500 J/cm² @Temperature -30.0 °C	2.38 ft-lb/in² @Temperature -22.0 °F	ISO 179
Electrical Properties	Metric	English	Comments
Dielectric Strength	21.0 kV/mm @Thickness 2.00 mm	533 kV/in @Thickness 0.0787 in	ASTM D149
Comparative Tracking Index	275 V @Thickness 3.20 mm	275 V @Thickness 0.126 in	Sol. B; IEC 112, UL 746A
	400 V @Thickness 3.20 mm	400 V @Thickness 0.126 in	Sol. A; IEC 112, UL 746A
Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	110 °C	230 °F	20,000 hr; IEC 216
Deflection Temperature at 0.46 MPa (66 psi)	250 °C	482 °F	ISO 75, ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	242 °C	468 °F	ISO 75, ASTM D648
Vicat Softening Point	240 °C	464 °F	49 N; ISO 306, ASTM D1525
	254 °C	489 °F	9.8 N; ISO 306, ASTM D1525
Flammability, UL94	V-0 @Thickness 0.800 mm	V-0 @Thickness 0.0315 in
	V-0 @Thickness 1.60 mm	V-0 @Thickness 0.0630 in
	V-0 @Thickness 3.20 mm	V-0 @Thickness 0.126 in
Oxygen Index	36 %	36 %	ASTM D2863
Glow Wire Test	825 °C @Thickness 0.800 mm	1520 °F @Thickness 0.0315 in	Glow Wire Ignition Temperature; IEC 695-2-13
	875 °C @Thickness 3.20 mm	1610 °F @Thickness 0.126 in	Glow Wire Ignition Temperature; IEC 695-2-13
	960 °C @Thickness 3.20 mm	1760 °F @Thickness 0.126 in	Glow Wire Flammability Index; IEC 694-2-12
	960 °C @Thickness 0.800 mm	1760 °F @Thickness 0.0315 in	Glow Wire Flammability Index; IEC 694-2-12
Processing Properties	Metric	English	Comments
Nozzle Temperature	275 - 285 °C	527 - 545 °F
Zone 1	260 - 280 °C	500 - 536 °F	hopper
Zone 2	260 - 280 °C	500 - 536 °F
Zone 3	270 - 280 °C	518 - 536 °F
Zone 4	275 - 285 °C	527 - 545 °F
Melt Temperature	275 - 290 °C	527 - 554 °F	Do not melt above 290°C
Mold Temperature	90.0 - 110 °C	194 - 230 °F	Preferred
Drying Temperature	80.0 - 85.0 °C	176 - 185 °F
Dry Time	4 hour	4 hour
Injection Pressure	70.0 - 100 MPa	10200 - 14500 psi
Descriptive Properties
Clamping Force	in tons, 0.7 times the projected surface area in cm2
Flammability Rating	SE	FMVSS No. 302, 355x100x1 mm
Heat Resistance - Ball Test	OK	at 125°C, IEC 309
	OK	at 165°C, IEC 309
Holding Pressure	90 MPa
Needle Test	OK	IEC 695-2-2, 1 or 2 mm