TPU ZHF 95AT3 物性表：
個別產品成品圖片
TPU ZHF 95AT3 物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 95 @Time 5.00 sec |
95 @Time 0.00139 hour |
ASTM D2240 |
| Tensile Strength | 10.3 MPa @Temperature 121 °C, Time 605000 sec |
1500 psi @Temperature 250 °F, Time 168 hour |
Air Oven |
| 11.7 MPa @Temperature 113 °C, Time 605000 sec |
1700 psi @Temperature 235 °F, Time 168 hour |
Air Oven | |
| 13.8 MPa @Temperature 100 °C, Time 605000 sec |
2000 psi @Temperature 212 °F, Time 168 hour |
IRM 902 Oil | |
| Tensile Strength, Ultimate | 13.8 MPa | 2000 psi | ASTM D412 |
| Elongation at Break | 360 % | 360 % | Ultimate; ASTM D412 |
| 270 % @Temperature 121 °C, Time 605000 sec |
270 % @Temperature 250 °F, Time 168 hour |
Air Oven | |
| 288 % @Temperature 100 °C, Time 605000 sec |
288 % @Temperature 212 °F, Time 168 hour |
IRM 902 Oil | |
| 324 % @Temperature 113 °C, Time 605000 sec |
324 % @Temperature 235 °F, Time 168 hour |
Air Oven | |
| 100% Modulus | 0.00960 GPa | 1.39 ksi | ASTM D412 |
| 300% Modulus | 0.0124 GPa | 1.80 ksi | ASTM D412 |
| Tear Strength | 15.8 kN/m | 90.0 pli | Trouser; ASTM D470 |
| Graves Tear Strength | 59.6 kN/m | 340 pli | Die C; ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 300 @Load 1.00 kg |
300 @Load 2.20 lb |
H-18 wheel; ASTM D3389 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 5.60e+12 ohm-cm | 5.60e+12 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 5.60e+14 ohm | 5.60e+14 ohm | ASTM D257 |
| Dielectric Constant | 4.5 @Frequency 1000 Hz |
4.5 @Frequency 1000 Hz |
ASTM D2520 |
| 5.7 @Frequency 1.00e+6 Hz |
5.7 @Frequency 1.00e+6 Hz |
ASTM D2520 | |
| Dissipation Factor | 0.040 @Frequency 1000 Hz |
0.040 @Frequency 1000 Hz |
ASTM D2520 |
| 0.050 @Frequency 1.00e+6 Hz |
0.050 @Frequency 1.00e+6 Hz |
ASTM D2520 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 175 °C | 347 °F | DSC |
| Glass Transition Temp, Tg | -30.0 °C | -22.0 °F | DSC |
| Flammability, UL94 | V-0 @Thickness 0.762 mm |
V-0 @Thickness 0.0300 in |
Vertical Flame Test; ASTM D3801 |
| Oxygen Index | 38 % | 38 % | ASTM D2863 |
| Processing Properties | Metric | English | Comments |
| Zone 1 | 160 °C | 320 °F | Extrusion |
| Zone 2 | 165 °C | 329 °F | Extrusion |
| Zone 3 | 170 °C | 338 °F | Extrusion |
| Zone 4 | 175 °C | 347 °F | Extrusion |
| Adapter Temperature | 180 °C | 356 °F | 5, Extrusion |
| Die Temperature | 180 °C | 356 °F | Zone 2, Extrusion |
| 180 °C | 356 °F | 6, Zone 1, Extrusion | |
| Drying Temperature | 82.0 °C | 180 °F | |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |
| Dew Point | -40.0 °C | -40.0 °F |
|
應用介紹：
1．薄膜和片材（TPU具較好耐磨性、抗刺穿性、抗撕裂性、彈性、粘合性）（TPU薄膜應用在冬季服裝、鞋類具有防寒、保暖、防水性能好等特性外還具有特別好的透氣性）
2．管材（TPU具有高伸長率，良好耐水解和抗微生物性、耐油性、優異機械性能，如作消防水管內襯，輸油管氣動軟管等）
3．鞋底，鞋邦等鞋材料（TPU具有突出耐磨性、抗刮性、耐刺穿性、抗縱向彎曲強度和低溫沖擊強度，其耐撕裂性和抗裂紋傳播性是所有塑料中最好的。如作溜冰、滑雪靴、運動鞋、特種功能鞋等）
4．電線、電纜、光纜護套（TPU具良好耐磨性、耐環境、耐候性、耐腐蝕性、絕緣性、彈性和低溫柔韌性等）
5．拉鏈片、高檔塑料表帶、表殼以及潛水表、禮品表等系列（TPU具有高彈、耐折、耐水性好手感舒適等）
6．機械制品和其它應用（如制造汽車部件、機械軸承、滾輪、輸送帶、橡塑篩網、工業膠管,墊圈,密封圈,游泳鏡,沖浪板,表帶,動物標牌,電器零部件,涂料,粘合劑,纖維等.)