特點：
1、綜合性能較好，沖擊強度較高，化學(xué)穩(wěn)定性，電性能良好.
2、與372有機玻璃的熔接性良好，制成雙色塑件，且可表面鍍鉻，噴漆處理.
3、有高抗沖、高耐熱、阻燃、增強、透明等級別。
4、流動性比HIPS差一點，比PMMA、PC等好，柔韌性好。
5、用途：適于制作一般機械零件，減磨耐磨零件，傳動零件和電訊零件.
6、同PVC（聚氯乙烯）一樣在屈折處會出現(xiàn)白化現(xiàn)象。
典型應(yīng)用范圍:
汽車內(nèi)外飾：儀表板，飾柱，儀表前蓋，格柵，內(nèi)外飾件 2.商務(wù)設(shè)備機殼和內(nèi)置部件：筆記本/臺式電腦，復(fù)印機，打印機，繪圖儀，顯示器 3.電信，移動電話外殼，附件以及智能卡（SIM卡）： 4.電器產(chǎn)品，電子產(chǎn)品外殼，電表罩和殼體，家用開關(guān)，插頭和插座，電纜電線管道 5.家用電器，如洗衣機，吹風(fēng)機，微波爐內(nèi)外部件等。
| 物性表： | |||
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ASTM D792 |
| Water Absorption at Saturation | 0.15 % | 0.15 % | ISO 62 |
| Melt Flow | 18 g/10 min @Load 2.16 kg, Temperature 260 °C |
18 g/10 min @Load 4.76 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 94.0 MPa | 13600 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 5.80 GPa | 841 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 140 MPa | 20300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 4.93 GPa | 715 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.850 J/cm | 1.59 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*3; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 38.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
21.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C @Thickness 3.20 mm |
203 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C @Thickness 3.20 mm |
194 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 99.0 °C | 210 °F | Rate B/120; ISO 306 |
| Flammability, UL94 | V-1 @Thickness 1.50 mm |
V-1 @Thickness 0.0591 in |
UL 94 |
| V-0 @Thickness 2.00 mm |
V-0 @Thickness 0.0787 in |
UL 94 | |